data_shelx
 
_audit_creation_method            'SHELXL-2014/7'
_shelx_SHELXL_version_number      '2014/7'
_chemical_name_systematic         ?
_chemical_name_common             ?
_chemical_melting_point           ?
_chemical_formula_moiety          ?
_chemical_formula_sum
 'Ca0.05 Mn0.91 Na4.87 O18 Si6 Zr0.88' 
_chemical_formula_weight          700.39

loop_
 _atom_type_symbol
 _atom_type_description
 _atom_type_scat_dispersion_real
 _atom_type_scat_dispersion_imag
 _atom_type_scat_source
 'Mn'  'Mn'   0.3368   0.7283
 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4'
 'Na'  'Na'   0.0362   0.0249
 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4'
 'O'  'O'   0.0106   0.0060
 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4'
 'Si'  'Si'   0.0817   0.0704
 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4'
 'Zr'  'Zr'  -2.9673   0.5597
 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4'
 'Ca'  'Ca'   0.2262   0.3064
 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4'
 
_space_group_crystal_system       trigonal
_space_group_IT_number            166
_space_group_name_H-M_alt         'R -3 m :H'
_space_group_name_Hall            '-R 3 2"'
 
_shelx_space_group_comment
;
The symmetry employed for this shelxl refinement is uniquely defined
by the following loop, which should always be used as a source of
symmetry information in preference to the above space-group names.
They are only intended as comments.
;
 
loop_
 _space_group_symop_operation_xyz
 'x, y, z'
 '-y, x-y, z'
 '-x+y, -x, z'
 'y, x, -z'
 'x-y, -y, -z'
 '-x, -x+y, -z'
 'x+2/3, y+1/3, z+1/3'
 '-y+2/3, x-y+1/3, z+1/3'
 '-x+y+2/3, -x+1/3, z+1/3'
 'y+2/3, x+1/3, -z+1/3'
 'x-y+2/3, -y+1/3, -z+1/3'
 '-x+2/3, -x+y+1/3, -z+1/3'
 'x+1/3, y+2/3, z+2/3'
 '-y+1/3, x-y+2/3, z+2/3'
 '-x+y+1/3, -x+2/3, z+2/3'
 'y+1/3, x+2/3, -z+2/3'
 'x-y+1/3, -y+2/3, -z+2/3'
 '-x+1/3, -x+y+2/3, -z+2/3'
 '-x, -y, -z'
 'y, -x+y, -z'
 'x-y, x, -z'
 '-y, -x, z'
 '-x+y, y, z'
 'x, x-y, z'
 '-x+2/3, -y+1/3, -z+1/3'
 'y+2/3, -x+y+1/3, -z+1/3'
 'x-y+2/3, x+1/3, -z+1/3'
 '-y+2/3, -x+1/3, z+1/3'
 '-x+y+2/3, y+1/3, z+1/3'
 'x+2/3, x-y+1/3, z+1/3'
 '-x+1/3, -y+2/3, -z+2/3'
 'y+1/3, -x+y+2/3, -z+2/3'
 'x-y+1/3, x+2/3, -z+2/3'
 '-y+1/3, -x+2/3, z+2/3'
 '-x+y+1/3, y+2/3, z+2/3'
 'x+1/3, x-y+2/3, z+2/3'
 
_cell_length_a                    10.294(6)
_cell_length_b                    10.294(6)
_cell_length_c                    13.115(8)
_cell_angle_alpha                 90
_cell_angle_beta                  90
_cell_angle_gamma                 120
_cell_volume                      1203.7(16)
_cell_formula_units_Z             3
_cell_measurement_temperature     296(2)
_cell_measurement_reflns_used     ?
_cell_measurement_theta_min       ?
_cell_measurement_theta_max       ?
 
_exptl_crystal_description        ?
_exptl_crystal_colour             ?
_exptl_crystal_density_meas       ?
_exptl_crystal_density_method     ?
_exptl_crystal_density_diffrn     2.898          
_exptl_crystal_F_000              1021
_exptl_transmission_factor_min    ?
_exptl_transmission_factor_max    ?
_exptl_crystal_size_max           ?
_exptl_crystal_size_mid           ?
_exptl_crystal_size_min           ?
_exptl_absorpt_coefficient_mu     1.988
_shelx_estimated_absorpt_T_min    ?
_shelx_estimated_absorpt_T_max    ?
_exptl_absorpt_correction_type    ?
_exptl_absorpt_correction_T_min   ?
_exptl_absorpt_correction_T_max   ?
_exptl_absorpt_process_details    ?
_exptl_absorpt_special_details    ?
_diffrn_ambient_temperature       296(2)
_diffrn_radiation_wavelength      0.71073
_diffrn_radiation_type            MoK\a
_diffrn_source                    ?
_diffrn_measurement_device_type   ?
_diffrn_measurement_method        ?
_diffrn_detector_area_resol_mean  ?
_diffrn_reflns_number             6753
_diffrn_reflns_av_unetI/netI      0.0200
_diffrn_reflns_av_R_equivalents   0.0383
_diffrn_reflns_limit_h_min        -16
_diffrn_reflns_limit_h_max        16
_diffrn_reflns_limit_k_min        -15
_diffrn_reflns_limit_k_max        16
_diffrn_reflns_limit_l_min        -18
_diffrn_reflns_limit_l_max        20
_diffrn_reflns_theta_min          2.763
_diffrn_reflns_theta_max          34.668
_diffrn_reflns_theta_full         25.242
_diffrn_measured_fraction_theta_max   0.997
_diffrn_measured_fraction_theta_full  0.997
_diffrn_reflns_Laue_measured_fraction_max    0.997
_diffrn_reflns_Laue_measured_fraction_full   0.997
_diffrn_reflns_point_group_measured_fraction_max   0.997
_diffrn_reflns_point_group_measured_fraction_full  0.997
_reflns_number_total              655
_reflns_number_gt                 578
_reflns_threshold_expression      'I > 2σ(I)'
_reflns_Friedel_coverage          0.000
_reflns_Friedel_fraction_max      .
_reflns_Friedel_fraction_full     .
 
_reflns_special_details
;
 Reflections were merged by SHELXL according to the crystal
 class for the calculation of statistics and refinement.
 
 _reflns_Friedel_fraction is defined as the number of unique
 Friedel pairs measured divided by the number that would be
 possible theoretically, ignoring centric projections and
 systematic absences.
;
 
_computing_data_collection        ?
_computing_cell_refinement        ?
_computing_data_reduction         ?
_computing_structure_solution     ?
_computing_structure_refinement 'SHELXL-2014/7 (Sheldrick, 2014)'
_computing_molecular_graphics     ?
_computing_publication_material   ?
_refine_special_details           ?
_refine_ls_structure_factor_coef  Fsqd
_refine_ls_matrix_type            full
_refine_ls_weighting_scheme       calc
_refine_ls_weighting_details
'w=1/[σ²(Fo²)+(0.0693P)²+9.9697P] where P=(Fo²+2Fc²)/3'
_atom_sites_solution_primary      ?
_atom_sites_solution_secondary    ?
_atom_sites_solution_hydrogens    .
_refine_ls_hydrogen_treatment     undef
_refine_ls_extinction_method      none
_refine_ls_extinction_coef        .
_refine_ls_number_reflns          655
_refine_ls_number_parameters      41
_refine_ls_number_restraints      0
_refine_ls_R_factor_all           0.0547
_refine_ls_R_factor_gt            0.0490
_refine_ls_wR_factor_ref          0.1463
_refine_ls_wR_factor_gt           0.1428
_refine_ls_goodness_of_fit_ref    1.172
_refine_ls_restrained_S_all       1.172
_refine_ls_shift/su_max           0.000
_refine_ls_shift/su_mean          0.000
 
loop_
 _atom_site_label
 _atom_site_type_symbol
 _atom_site_fract_x
 _atom_site_fract_y
 _atom_site_fract_z
 _atom_site_U_iso_or_equiv
 _atom_site_adp_type
 _atom_site_occupancy
 _atom_site_site_symmetry_order  
 _atom_site_calc_flag
 _atom_site_refinement_flags_posn
 _atom_site_refinement_flags_adp
 _atom_site_refinement_flags_occupancy
 _atom_site_disorder_assembly
 _atom_site_disorder_group
Zr Zr 0.3333 0.6667 0.1667 0.0163(3) Uani 0.892(7) 12 d S T . . .
Si Si 0.15049(7) 0.30099(13) 0.06698(9) 0.0195(3) Uani 1 2 d S T P . .
NaA Na 0.1667 0.3333 0.3333 0.0347(11) Uani 0.953(13) 4 d S T P . .
MnA Mn 0.1667 0.3333 0.3333 0.0347(11) Uani 0.047(13) 4 d S T P . .
NaC Na 0.0000 0.0000 0.2512(2) 0.0211(8) Uani 1.039(16) 6 d S T P . .
O1 O 0.24126(19) 0.4825(4) 0.0687(3) 0.0337(8) Uani 1 2 d S T P . .
O2 O 0.1113(3) 0.2226(5) 0.1741(3) 0.0457(11) Uani 1 2 d S T P . .
O3 O 0.2549(4) 0.2549(4) 0.0000 0.0388(9) Uani 1 2 d S T P . .
OB O -0.1667 0.1667 0.1667 0.0288(14) Uani 0.89(4) 4 d S T P . .
NaB Na -0.1667 0.1667 0.1667 0.0288(14) Uani 0.11(4) 4 d S T P . .
 
 
_geom_special_details
;
 All esds (except the esd in the dihedral angle between two l.s. planes)
 are estimated using the full covariance matrix.  The cell esds are taken
 into account individually in the estimation of esds in distances, angles
 and torsion angles; correlations between esds in cell parameters are only
 used when they are defined by crystal symmetry.  An approximate (isotropic)
 treatment of cell esds is used for estimating esds involving l.s. planes.
;
 
loop_
 _geom_bond_atom_site_label_1
 _geom_bond_atom_site_label_2
 _geom_bond_distance
 _geom_bond_site_symmetry_2
 _geom_bond_publ_flag
Zr O1 2.085(3) 27 ?
Zr O1 2.085(3) 3_565 ?
Zr O1 2.085(3) . ?
Zr O1 2.085(3) 2_665 ?
Zr O1 2.085(3) 25_565 ?
Zr O1 2.085(3) 26_455 ?
Zr NaC 3.264(4) 31 ?
Zr NaC 3.264(4) 13_554 ?
Zr NaA 3.6891(16) 14_554 ?
Zr NaA 3.6891(16) 2_665 ?
Zr NaA 3.6891(16) . ?
Zr NaA 3.6891(16) 13_554 ?
Si O2 1.570(4) . ?
Si O1 1.618(4) . ?
Si O3 1.6316(12) . ?
Si O3 1.6316(12) 21 ?
Si NaB 3.078(2) 14_554 ?
Si OB 3.078(2) 14_554 ?
Si OB 3.1252(17) . ?
Si NaB 3.1253(17) 3 ?
Si OB 3.1253(17) 3 ?
Si NaA 3.2470(19) 15_554 ?
Si NaA 3.2470(19) 14_554 ?
NaA O2 2.310(4) . ?
NaA O2 2.310(4) 31 ?
NaA O3 2.523(4) 8 ?
NaA O3 2.523(4) 26_455 ?
NaA O1 2.731(2) 8 ?
NaA O1 2.731(2) 27 ?
NaA O1 2.731(2) 9_455 ?
NaA O1 2.731(2) 26_455 ?
NaA NaC 3.1611(19) 31 ?
NaA NaC 3.1612(19) . ?
NaA Si 3.2470(19) 8 ?
NaA Si 3.2470(19) 27 ?
NaC O2 2.226(5) 2 ?
NaC O2 2.226(5) 3 ?
NaC O2 2.226(5) . ?
NaC O1 2.571(5) 8 ?
NaC O1 2.571(5) 7_445 ?
NaC O1 2.571(5) 9_455 ?
NaC MnA 3.1611(19) 3 ?
NaC NaA 3.1611(19) 3 ?
NaC NaA 3.1612(19) 2 ?
NaC MnA 3.1612(19) 2 ?
O1 NaC 2.571(5) 13_554 ?
O1 O3 2.579(4) . ?
O1 O3 2.579(4) 21 ?
O1 O2 2.699(6) . ?
O1 MnA 2.731(2) 15_554 ?
O1 NaA 2.731(2) 15_554 ?
O1 MnA 2.731(2) 14_554 ?
O1 NaA 2.731(2) 14_554 ?
O1 O1 2.844(6) 2_665 ?
O1 O1 2.844(6) 3_565 ?
O2 OB 2.6232(18) . ?
O2 NaB 2.6233(18) 3 ?
O2 OB 2.6233(18) 3 ?
O2 O3 2.650(4) 21 ?
O2 O3 2.650(4) . ?
O2 O3 3.420(4) 8 ?
O3 Si 1.6317(12) 20 ?
O3 MnA 2.523(4) 15_554 ?
O3 NaA 2.523(4) 15_554 ?
O3 O1 2.579(4) 20 ?
O3 O3 2.625(4) 21 ?
O3 O3 2.625(4) 20 ?
O3 NaB 2.6436(12) 3 ?
O3 OB 2.6436(12) 3 ?
O3 NaB 2.6436(12) 14_554 ?
O3 OB 2.6436(12) 14_554 ?
OB O2 2.6232(18) 2 ?
OB O2 2.6233(18) 26_455 ?
OB O2 2.6233(18) 25_455 ?
OB O3 2.6436(12) 2 ?
OB O3 2.6436(12) 21 ?
OB O3 2.6436(12) 26_455 ?
OB O3 2.6436(12) 9_455 ?
OB Si 3.078(2) 21 ?
OB Si 3.078(2) 9_455 ?
OB Si 3.1252(17) 2 ?
OB Si 3.1252(17) 26_455 ?
 
loop_
 _geom_angle_atom_site_label_1
 _geom_angle_atom_site_label_2
 _geom_angle_atom_site_label_3
 _geom_angle
 _geom_angle_site_symmetry_1
 _geom_angle_site_symmetry_3
 _geom_angle_publ_flag
O1 Zr O1 180.0 27 3_565 ?
O1 Zr O1 94.02(16) 27 . ?
O1 Zr O1 85.98(17) 3_565 . ?
O1 Zr O1 94.02(17) 27 2_665 ?
O1 Zr O1 85.98(17) 3_565 2_665 ?
O1 Zr O1 85.98(16) . 2_665 ?
O1 Zr O1 85.98(17) 27 25_565 ?
O1 Zr O1 94.01(16) 3_565 25_565 ?
O1 Zr O1 180.00(17) . 25_565 ?
O1 Zr O1 94.02(17) 2_665 25_565 ?
O1 Zr O1 85.98(17) 27 26_455 ?
O1 Zr O1 94.01(17) 3_565 26_455 ?
O1 Zr O1 94.02(17) . 26_455 ?
O1 Zr O1 180.0 2_665 26_455 ?
O1 Zr O1 85.98(17) 25_565 26_455 ?
O1 Zr NaC 51.94(11) 27 31 ?
O1 Zr NaC 128.06(11) 3_565 31 ?
O1 Zr NaC 128.06(11) . 31 ?
O1 Zr NaC 128.06(11) 2_665 31 ?
O1 Zr NaC 51.94(11) 25_565 31 ?
O1 Zr NaC 51.94(11) 26_455 31 ?
O1 Zr NaC 128.06(11) 27 13_554 ?
O1 Zr NaC 51.94(11) 3_565 13_554 ?
O1 Zr NaC 51.94(11) . 13_554 ?
O1 Zr NaC 51.94(11) 2_665 13_554 ?
O1 Zr NaC 128.06(11) 25_565 13_554 ?
O1 Zr NaC 128.06(11) 26_455 13_554 ?
NaC Zr NaC 180.0 31 13_554 ?
O1 Zr NaA 133.03(4) 27 14_554 ?
O1 Zr NaA 46.97(4) 3_565 14_554 ?
O1 Zr NaA 46.97(4) . 14_554 ?
O1 Zr NaA 105.61(12) 2_665 14_554 ?
O1 Zr NaA 133.03(4) 25_565 14_554 ?
O1 Zr NaA 74.39(12) 26_455 14_554 ?
NaC Zr NaA 126.34(2) 31 14_554 ?
NaC Zr NaA 53.66(2) 13_554 14_554 ?
O1 Zr NaA 46.97(4) 27 2_665 ?
O1 Zr NaA 133.03(4) 3_565 2_665 ?
O1 Zr NaA 133.03(4) . 2_665 ?
O1 Zr NaA 74.39(12) 2_665 2_665 ?
O1 Zr NaA 46.97(4) 25_565 2_665 ?
O1 Zr NaA 105.60(12) 26_455 2_665 ?
NaC Zr NaA 53.66(2) 31 2_665 ?
NaC Zr NaA 126.34(2) 13_554 2_665 ?
NaA Zr NaA 180.0 14_554 2_665 ?
O1 Zr NaA 46.97(4) 27 . ?
O1 Zr NaA 133.03(4) 3_565 . ?
O1 Zr NaA 74.39(12) . . ?
O1 Zr NaA 133.03(4) 2_665 . ?
O1 Zr NaA 105.61(12) 25_565 . ?
O1 Zr NaA 46.97(4) 26_455 . ?
NaC Zr NaA 53.66(2) 31 . ?
NaC Zr NaA 126.34(2) 13_554 . ?
NaA Zr NaA 91.53(3) 14_554 . ?
NaA Zr NaA 88.47(3) 2_665 . ?
O1 Zr NaA 133.03(4) 27 13_554 ?
O1 Zr NaA 46.97(4) 3_565 13_554 ?
O1 Zr NaA 105.61(12) . 13_554 ?
O1 Zr NaA 46.97(4) 2_665 13_554 ?
O1 Zr NaA 74.39(12) 25_565 13_554 ?
O1 Zr NaA 133.03(4) 26_455 13_554 ?
NaC Zr NaA 126.34(2) 31 13_554 ?
NaC Zr NaA 53.66(2) 13_554 13_554 ?
NaA Zr NaA 88.47(3) 14_554 13_554 ?
NaA Zr NaA 91.53(3) 2_665 13_554 ?
NaA Zr NaA 180.0 . 13_554 ?
O2 Si O1 115.7(2) . . ?
O2 Si O3 111.71(11) . . ?
O1 Si O3 105.01(16) . . ?
O2 Si O3 111.71(11) . 21 ?
O1 Si O3 105.01(16) . 21 ?
O3 Si O3 107.08(18) . 21 ?
O2 Si NaB 158.92(18) . 14_554 ?
O1 Si NaB 85.41(15) . 14_554 ?
O3 Si NaB 59.17(4) . 14_554 ?
O3 Si NaB 59.17(4) 21 14_554 ?
O2 Si OB 158.92(18) . 14_554 ?
O1 Si OB 85.41(15) . 14_554 ?
O3 Si OB 59.17(4) . 14_554 ?
O3 Si OB 59.17(4) 21 14_554 ?
NaB Si OB 0.0 14_554 14_554 ?
O2 Si OB 56.96(4) . . ?
O1 Si OB 112.17(7) . . ?
O3 Si OB 142.29(15) . . ?
O3 Si OB 57.76(4) 21 . ?
NaB Si OB 116.9 14_554 . ?
OB Si OB 116.90(3) 14_554 . ?
O2 Si NaB 56.96(4) . 3 ?
O1 Si NaB 112.17(7) . 3 ?
O3 Si NaB 57.76(4) . 3 ?
O3 Si NaB 142.29(15) 21 3 ?
NaB Si NaB 116.90(3) 14_554 3 ?
OB Si NaB 116.90(3) 14_554 3 ?
OB Si NaB 110.9 . 3 ?
O2 Si OB 56.96(4) . 3 ?
O1 Si OB 112.17(7) . 3 ?
O3 Si OB 57.76(4) . 3 ?
O3 Si OB 142.29(15) 21 3 ?
NaB Si OB 116.9 14_554 3 ?
OB Si OB 116.90(3) 14_554 3 ?
OB Si OB 110.87(4) . 3 ?
NaB Si OB 0.0 3 3 ?
O2 Si NaA 119.05(8) . 15_554 ?
O1 Si NaA 57.13(5) . 15_554 ?
O3 Si NaA 49.79(14) . 15_554 ?
O3 Si NaA 129.00(7) 21 15_554 ?
NaB Si NaA 71.30(2) 14_554 15_554 ?
OB Si NaA 71.30(2) 14_554 15_554 ?
OB Si NaA 167.23(4) . 15_554 ?
NaB Si NaA 70.721(16) 3 15_554 ?
OB Si NaA 70.721(16) 3 15_554 ?
O2 Si NaA 119.05(8) . 14_554 ?
O1 Si NaA 57.13(5) . 14_554 ?
O3 Si NaA 129.00(7) . 14_554 ?
O3 Si NaA 49.79(14) 21 14_554 ?
NaB Si NaA 71.31(2) 14_554 14_554 ?
OB Si NaA 71.31(2) 14_554 14_554 ?
OB Si NaA 70.722(16) . 14_554 ?
NaB Si NaA 167.23(4) 3 14_554 ?
OB Si NaA 167.23(4) 3 14_554 ?
NaA Si NaA 104.86(3) 15_554 14_554 ?
O2 NaA O2 180.00(7) . 31 ?
O2 NaA O3 90.0 . 8 ?
O2 NaA O3 89.998(1) 31 8 ?
O2 NaA O3 90.0 . 26_455 ?
O2 NaA O3 90.0 31 26_455 ?
O3 NaA O3 180.0 8 26_455 ?
O2 NaA O1 87.78(13) . 8 ?
O2 NaA O1 92.22(13) 31 8 ?
O3 NaA O1 58.63(7) 8 8 ?
O3 NaA O1 121.37(7) 26_455 8 ?
O2 NaA O1 92.22(13) . 27 ?
O2 NaA O1 87.78(13) 31 27 ?
O3 NaA O1 58.63(7) 8 27 ?
O3 NaA O1 121.37(7) 26_455 27 ?
O1 NaA O1 117.25(14) 8 27 ?
O2 NaA O1 87.78(13) . 9_455 ?
O2 NaA O1 92.22(13) 31 9_455 ?
O3 NaA O1 121.37(7) 8 9_455 ?
O3 NaA O1 58.63(7) 26_455 9_455 ?
O1 NaA O1 62.75(14) 8 9_455 ?
O1 NaA O1 180.0 27 9_455 ?
O2 NaA O1 92.22(13) . 26_455 ?
O2 NaA O1 87.78(13) 31 26_455 ?
O3 NaA O1 121.37(7) 8 26_455 ?
O3 NaA O1 58.63(7) 26_455 26_455 ?
O1 NaA O1 180.0 8 26_455 ?
O1 NaA O1 62.75(14) 27 26_455 ?
O1 NaA O1 117.25(14) 9_455 26_455 ?
O2 NaA NaC 135.25(12) . 31 ?
O2 NaA NaC 44.75(12) 31 31 ?
O3 NaA NaC 90.0 8 31 ?
O3 NaA NaC 90.000(1) 26_455 31 ?
O1 NaA NaC 128.90(9) 8 31 ?
O1 NaA NaC 51.10(9) 27 31 ?
O1 NaA NaC 128.90(9) 9_455 31 ?
O1 NaA NaC 51.10(9) 26_455 31 ?
O2 NaA NaC 44.75(12) . . ?
O2 NaA NaC 135.25(12) 31 . ?
O3 NaA NaC 90.0 8 . ?
O3 NaA NaC 90.0 26_455 . ?
O1 NaA NaC 51.10(9) 8 . ?
O1 NaA NaC 128.90(9) 27 . ?
O1 NaA NaC 51.10(9) 9_455 . ?
O1 NaA NaC 128.90(9) 26_455 . ?
NaC NaA NaC 180.0 31 . ?
O2 NaA Si 93.89(6) . 8 ?
O2 NaA Si 86.11(6) 31 8 ?
O3 NaA Si 29.60(2) 8 8 ?
O3 NaA Si 150.40(2) 26_455 8 ?
O1 NaA Si 29.85(7) 8 8 ?
O1 NaA Si 87.82(7) 27 8 ?
O1 NaA Si 92.18(7) 9_455 8 ?
O1 NaA Si 150.15(7) 26_455 8 ?
NaC NaA Si 107.23(3) 31 8 ?
NaC NaA Si 72.77(3) . 8 ?
O2 NaA Si 86.11(6) . 27 ?
O2 NaA Si 93.89(6) 31 27 ?
O3 NaA Si 29.60(2) 8 27 ?
O3 NaA Si 150.40(2) 26_455 27 ?
O1 NaA Si 87.82(7) 8 27 ?
O1 NaA Si 29.85(7) 27 27 ?
O1 NaA Si 150.15(7) 9_455 27 ?
O1 NaA Si 92.18(7) 26_455 27 ?
NaC NaA Si 72.77(3) 31 27 ?
NaC NaA Si 107.23(3) . 27 ?
Si NaA Si 59.19(4) 8 27 ?
O2 NaC O2 101.03(15) 2 3 ?
O2 NaC O2 101.03(15) 2 . ?
O2 NaC O2 101.03(15) 3 . ?
O2 NaC O1 156.67(17) 2 8 ?
O2 NaC O1 93.70(10) 3 8 ?
O2 NaC O1 93.70(10) . 8 ?
O2 NaC O1 93.70(10) 2 7_445 ?
O2 NaC O1 93.70(10) 3 7_445 ?
O2 NaC O1 156.67(17) . 7_445 ?
O1 NaC O1 67.15(14) 8 7_445 ?
O2 NaC O1 93.70(10) 2 9_455 ?
O2 NaC O1 156.67(17) 3 9_455 ?
O2 NaC O1 93.70(10) . 9_455 ?
O1 NaC O1 67.15(14) 8 9_455 ?
O1 NaC O1 67.15(14) 7_445 9_455 ?
O2 NaC MnA 125.000(16) 2 3 ?
O2 NaC MnA 46.92(11) 3 3 ?
O2 NaC MnA 124.999(16) . 3 ?
O1 NaC MnA 55.77(3) 8 3 ?
O1 NaC MnA 55.77(3) 7_445 3 ?
O1 NaC MnA 109.75(13) 9_455 3 ?
O2 NaC NaA 125.000(16) 2 3 ?
O2 NaC NaA 46.92(11) 3 3 ?
O2 NaC NaA 124.999(16) . 3 ?
O1 NaC NaA 55.77(3) 8 3 ?
O1 NaC NaA 55.77(3) 7_445 3 ?
O1 NaC NaA 109.75(13) 9_455 3 ?
MnA NaC NaA 0.0 3 3 ?
O2 NaC NaA 124.999(17) 2 . ?
O2 NaC NaA 124.999(16) 3 . ?
O2 NaC NaA 46.91(11) . . ?
O1 NaC NaA 55.77(3) 8 . ?
O1 NaC NaA 109.75(13) 7_445 . ?
O1 NaC NaA 55.77(3) 9_455 . ?
MnA NaC NaA 109.0 3 . ?
NaA NaC NaA 109.00(5) 3 . ?
O2 NaC NaA 46.92(11) 2 2 ?
O2 NaC NaA 125.000(16) 3 2 ?
O2 NaC NaA 124.999(16) . 2 ?
O1 NaC NaA 109.75(13) 8 2 ?
O1 NaC NaA 55.77(3) 7_445 2 ?
O1 NaC NaA 55.77(3) 9_455 2 ?
MnA NaC NaA 109.0 3 2 ?
NaA NaC NaA 109.00(5) 3 2 ?
NaA NaC NaA 109.00(5) . 2 ?
O2 NaC MnA 46.92(11) 2 2 ?
O2 NaC MnA 125.000(16) 3 2 ?
O2 NaC MnA 124.999(16) . 2 ?
O1 NaC MnA 109.75(13) 8 2 ?
O1 NaC MnA 55.77(3) 7_445 2 ?
O1 NaC MnA 55.77(3) 9_455 2 ?
MnA NaC MnA 109.00(5) 3 2 ?
NaA NaC MnA 109.00(5) 3 2 ?
NaA NaC MnA 109.0 . 2 ?
NaA NaC MnA 0.0 2 2 ?
Si O1 Zr 142.7(2) . . ?
Si O1 NaC 128.9(2) . 13_554 ?
Zr O1 NaC 88.37(14) . 13_554 ?
Si O1 O3 37.67(10) . . ?
Zr O1 O3 146.60(10) . . ?
NaC O1 O3 103.52(14) 13_554 . ?
Si O1 O3 37.67(10) . 21 ?
Zr O1 O3 146.60(10) . 21 ?
NaC O1 O3 103.52(14) 13_554 21 ?
O3 O1 O3 61.18(16) . 21 ?
Si O1 O2 31.62(12) . . ?
Zr O1 O2 111.11(19) . . ?
NaC O1 O2 160.52(18) 13_554 . ?
O3 O1 O2 60.23(12) . . ?
O3 O1 O2 60.23(12) 21 . ?
Si O1 MnA 93.01(8) . 15_554 ?
Zr O1 MnA 99.11(8) . 15_554 ?
NaC O1 MnA 73.13(8) 13_554 15_554 ?
O3 O1 MnA 56.65(9) . 15_554 ?
O3 O1 MnA 114.16(13) 21 15_554 ?
O2 O1 MnA 102.59(8) . 15_554 ?
Si O1 NaA 93.01(8) . 15_554 ?
Zr O1 NaA 99.11(8) . 15_554 ?
NaC O1 NaA 73.13(8) 13_554 15_554 ?
O3 O1 NaA 56.65(9) . 15_554 ?
O3 O1 NaA 114.16(13) 21 15_554 ?
O2 O1 NaA 102.59(8) . 15_554 ?
MnA O1 NaA 0.0 15_554 15_554 ?
Si O1 MnA 93.01(8) . 14_554 ?
Zr O1 MnA 99.11(8) . 14_554 ?
NaC O1 MnA 73.13(8) 13_554 14_554 ?
O3 O1 MnA 114.16(13) . 14_554 ?
O3 O1 MnA 56.65(9) 21 14_554 ?
O2 O1 MnA 102.59(8) . 14_554 ?
MnA O1 MnA 140.90(16) 15_554 14_554 ?
NaA O1 MnA 140.90(16) 15_554 14_554 ?
Si O1 NaA 93.01(8) . 14_554 ?
Zr O1 NaA 99.11(8) . 14_554 ?
NaC O1 NaA 73.13(8) 13_554 14_554 ?
O3 O1 NaA 114.16(13) . 14_554 ?
O3 O1 NaA 56.65(9) 21 14_554 ?
O2 O1 NaA 102.59(8) . 14_554 ?
MnA O1 NaA 140.9 15_554 14_554 ?
NaA O1 NaA 140.90(16) 15_554 14_554 ?
MnA O1 NaA 0.0 14_554 14_554 ?
Si O1 O1 149.991(4) . 2_665 ?
Zr O1 O1 47.01(8) . 2_665 ?
NaC O1 O1 56.42(7) 13_554 2_665 ?
O3 O1 O1 115.27(9) . 2_665 ?
O3 O1 O1 159.36(9) 21 2_665 ?
O2 O1 O1 138.04(8) . 2_665 ?
MnA O1 O1 58.63(7) 15_554 2_665 ?
NaA O1 O1 58.63(7) 15_554 2_665 ?
MnA O1 O1 114.94(7) 14_554 2_665 ?
NaA O1 O1 114.94(7) 14_554 2_665 ?
Si O1 O1 149.991(4) . 3_565 ?
Zr O1 O1 47.01(8) . 3_565 ?
NaC O1 O1 56.42(7) 13_554 3_565 ?
O3 O1 O1 159.36(9) . 3_565 ?
O3 O1 O1 115.27(9) 21 3_565 ?
O2 O1 O1 138.04(8) . 3_565 ?
MnA O1 O1 114.94(7) 15_554 3_565 ?
NaA O1 O1 114.94(7) 15_554 3_565 ?
MnA O1 O1 58.63(7) 14_554 3_565 ?
NaA O1 O1 58.63(7) 14_554 3_565 ?
O1 O1 O1 60.0 2_665 3_565 ?
Si O2 NaC 143.4(3) . . ?
Si O2 NaA 128.2(3) . . ?
NaC O2 NaA 88.34(15) . . ?
Si O2 OB 92.93(8) . . ?
NaC O2 OB 81.24(10) . . ?
NaA O2 OB 96.60(8) . . ?
Si O2 NaB 92.93(8) . 3 ?
NaC O2 NaB 81.24(10) . 3 ?
NaA O2 NaB 96.60(8) . 3 ?
OB O2 NaB 157.7 . 3 ?
Si O2 OB 92.93(8) . 3 ?
NaC O2 OB 81.24(10) . 3 ?
NaA O2 OB 96.60(8) . 3 ?
OB O2 OB 157.7(2) . 3 ?
NaB O2 OB 0.0 3 3 ?
Si O2 O3 34.89(7) . 21 ?
NaC O2 O3 119.22(18) . 21 ?
NaA O2 O3 137.10(17) . 21 ?
OB O2 O3 60.17(5) . 21 ?
NaB O2 O3 118.32(13) 3 21 ?
OB O2 O3 118.32(13) 3 21 ?
Si O2 O3 34.89(7) . . ?
NaC O2 O3 119.22(17) . . ?
NaA O2 O3 137.10(17) . . ?
OB O2 O3 118.32(13) . . ?
NaB O2 O3 60.17(5) 3 . ?
OB O2 O3 60.17(5) 3 . ?
O3 O2 O3 59.37(11) 21 . ?
Si O2 O1 32.72(14) . . ?
NaC O2 O1 176.1(2) . . ?
NaA O2 O1 95.52(18) . . ?
OB O2 O1 98.28(9) . . ?
NaB O2 O1 98.28(9) 3 . ?
OB O2 O1 98.28(9) 3 . ?
O3 O2 O1 57.63(12) 21 . ?
O3 O2 O1 57.63(12) . . ?
Si O2 O3 114.70(14) . 8 ?
NaC O2 O3 88.88(10) . 8 ?
NaA O2 O3 47.52(7) . 8 ?
OB O2 O3 143.25(13) . 8 ?
NaB O2 O3 49.76(6) 3 8 ?
OB O2 O3 49.76(6) 3 8 ?
O3 O2 O3 149.31(14) 21 8 ?
O3 O2 O3 97.44(6) . 8 ?
O1 O2 O3 93.72(12) . 8 ?
Si O3 Si 158.8(3) . 20 ?
Si O3 MnA 100.62(14) . 15_554 ?
Si O3 MnA 100.62(14) 20 15_554 ?
Si O3 NaA 100.62(14) . 15_554 ?
Si O3 NaA 100.62(14) 20 15_554 ?
MnA O3 NaA 0.0 15_554 15_554 ?
Si O3 O1 37.32(10) . . ?
Si O3 O1 162.3(2) 20 . ?
MnA O3 O1 64.73(9) 15_554 . ?
NaA O3 O1 64.73(9) 15_554 . ?
Si O3 O1 162.3(2) . 20 ?
Si O3 O1 37.32(10) 20 20 ?
MnA O3 O1 64.73(9) 15_554 20 ?
NaA O3 O1 64.73(9) 15_554 20 ?
O1 O3 O1 129.45(19) . 20 ?
Si O3 O3 36.46(9) . 21 ?
Si O3 O3 128.32(12) 20 21 ?
MnA O3 O3 120.0 15_554 21 ?
NaA O3 O3 120.0 15_554 21 ?
O1 O3 O3 59.41(8) . 21 ?
O1 O3 O3 159.36(9) 20 21 ?
Si O3 O3 128.32(12) . 20 ?
Si O3 O3 36.46(9) 20 20 ?
MnA O3 O3 120.0 15_554 20 ?
NaA O3 O3 120.0 15_554 20 ?
O1 O3 O3 159.36(9) . 20 ?
O1 O3 O3 59.41(8) 20 20 ?
O3 O3 O3 120.0 21 20 ?
Si O3 NaB 90.77(6) . 3 ?
Si O3 NaB 88.82(6) 20 3 ?
MnA O3 NaB 91.10(9) 15_554 3 ?
NaA O3 NaB 91.10(9) 15_554 3 ?
O1 O3 NaB 100.85(10) . 3 ?
O1 O3 NaB 80.10(9) 20 3 ?
O3 O3 NaB 118.50(5) 21 3 ?
O3 O3 NaB 60.24(5) 20 3 ?
Si O3 OB 90.77(6) . 3 ?
Si O3 OB 88.82(6) 20 3 ?
MnA O3 OB 91.10(9) 15_554 3 ?
NaA O3 OB 91.10(9) 15_554 3 ?
O1 O3 OB 100.85(10) . 3 ?
O1 O3 OB 80.10(9) 20 3 ?
O3 O3 OB 118.50(5) 21 3 ?
O3 O3 OB 60.24(5) 20 3 ?
NaB O3 OB 0.0 3 3 ?
Si O3 NaB 88.82(6) . 14_554 ?
Si O3 NaB 90.77(6) 20 14_554 ?
MnA O3 NaB 91.10(9) 15_554 14_554 ?
NaA O3 NaB 91.10(9) 15_554 14_554 ?
O1 O3 NaB 80.11(9) . 14_554 ?
O1 O3 NaB 100.85(10) 20 14_554 ?
O3 O3 NaB 60.24(5) 21 14_554 ?
O3 O3 NaB 118.50(5) 20 14_554 ?
NaB O3 NaB 177.79(17) 3 14_554 ?
OB O3 NaB 177.79(17) 3 14_554 ?
Si O3 OB 88.82(6) . 14_554 ?
Si O3 OB 90.77(6) 20 14_554 ?
MnA O3 OB 91.10(9) 15_554 14_554 ?
NaA O3 OB 91.10(9) 15_554 14_554 ?
O1 O3 OB 80.11(9) . 14_554 ?
O1 O3 OB 100.85(10) 20 14_554 ?
O3 O3 OB 60.24(5) 21 14_554 ?
O3 O3 OB 118.50(5) 20 14_554 ?
NaB O3 OB 177.8 3 14_554 ?
OB O3 OB 177.79(17) 3 14_554 ?
NaB O3 OB 0.0 14_554 14_554 ?
O2 OB O2 81.84(19) 2 . ?
O2 OB O2 180.0 2 26_455 ?
O2 OB O2 98.16(19) . 26_455 ?
O2 OB O2 98.16(19) 2 25_455 ?
O2 OB O2 180.0 . 25_455 ?
O2 OB O2 81.84(19) 26_455 25_455 ?
O2 OB O3 60.41(9) 2 2 ?
O2 OB O3 99.01(12) . 2 ?
O2 OB O3 119.59(9) 26_455 2 ?
O2 OB O3 81.00(12) 25_455 2 ?
O2 OB O3 99.01(12) 2 21 ?
O2 OB O3 60.41(9) . 21 ?
O2 OB O3 81.00(12) 26_455 21 ?
O2 OB O3 119.59(9) 25_455 21 ?
O3 OB O3 59.52(10) 2 21 ?
O2 OB O3 119.59(9) 2 26_455 ?
O2 OB O3 80.99(12) . 26_455 ?
O2 OB O3 60.41(9) 26_455 26_455 ?
O2 OB O3 99.00(12) 25_455 26_455 ?
O3 OB O3 180.0 2 26_455 ?
O3 OB O3 120.48(10) 21 26_455 ?
O2 OB O3 81.00(12) 2 9_455 ?
O2 OB O3 119.59(9) . 9_455 ?
O2 OB O3 99.00(12) 26_455 9_455 ?
O2 OB O3 60.41(9) 25_455 9_455 ?
O3 OB O3 120.48(10) 2 9_455 ?
O3 OB O3 180.0 21 9_455 ?
O3 OB O3 59.52(10) 26_455 9_455 ?
O2 OB Si 88.08(8) 2 21 ?
O2 OB Si 88.08(8) . 21 ?
O2 OB Si 91.92(8) 26_455 21 ?
O2 OB Si 91.92(8) 25_455 21 ?
O3 OB Si 32.01(3) 2 21 ?
O3 OB Si 32.01(3) 21 21 ?
O3 OB Si 148.00(3) 26_455 21 ?
O3 OB Si 147.99(3) 9_455 21 ?
O2 OB Si 91.92(8) 2 9_455 ?
O2 OB Si 91.92(8) . 9_455 ?
O2 OB Si 88.08(8) 26_455 9_455 ?
O2 OB Si 88.08(8) 25_455 9_455 ?
O3 OB Si 148.00(3) 2 9_455 ?
O3 OB Si 148.00(3) 21 9_455 ?
O3 OB Si 32.00(3) 26_455 9_455 ?
O3 OB Si 32.00(3) 9_455 9_455 ?
Si OB Si 180.0 21 9_455 ?
O2 OB Si 30.11(8) 2 2 ?
O2 OB Si 96.26(10) . 2 ?
O2 OB Si 149.89(8) 26_455 2 ?
O2 OB Si 83.74(10) 25_455 2 ?
O3 OB Si 31.47(2) 2 2 ?
O3 OB Si 83.41(8) 21 2 ?
O3 OB Si 148.53(2) 26_455 2 ?
O3 OB Si 96.59(8) 9_455 2 ?
Si OB Si 62.26(3) 21 2 ?
Si OB Si 117.74(3) 9_455 2 ?
O2 OB Si 149.89(8) 2 26_455 ?
O2 OB Si 83.74(10) . 26_455 ?
O2 OB Si 30.11(8) 26_455 26_455 ?
O2 OB Si 96.26(10) 25_455 26_455 ?
O3 OB Si 148.53(2) 2 26_455 ?
O3 OB Si 96.59(8) 21 26_455 ?
O3 OB Si 31.47(2) 26_455 26_455 ?
O3 OB Si 83.41(8) 9_455 26_455 ?
Si OB Si 117.74(3) 21 26_455 ?
Si OB Si 62.26(3) 9_455 26_455 ?
Si OB Si 180.0 2 26_455 ?
 
loop_
 _geom_torsion_atom_site_label_1
 _geom_torsion_atom_site_label_2
 _geom_torsion_atom_site_label_3
 _geom_torsion_atom_site_label_4
 _geom_torsion
 _geom_torsion_site_symmetry_1
 _geom_torsion_site_symmetry_2
 _geom_torsion_site_symmetry_3
 _geom_torsion_site_symmetry_4
 _geom_torsion_publ_flag
O2 Si O1 Zr 0.000(1) . . . . ?
O3 Si O1 Zr -123.63(7) . . . . ?
O3 Si O1 Zr 123.63(7) 21 . . . ?
NaB Si O1 Zr 180.001(0) 14_554 . . . ?
OB Si O1 Zr 180.001(0) 14_554 . . . ?
OB Si O1 Zr 62.78(6) . . . . ?
NaB Si O1 Zr -62.78(6) 3 . . . ?
OB Si O1 Zr -62.78(6) 3 . . . ?
NaA Si O1 Zr -109.33(9) 15_554 . . . ?
NaA Si O1 Zr 109.33(9) 14_554 . . . ?
O2 Si O1 NaC 179.999(0) . . . 13_554 ?
O3 Si O1 NaC 56.37(7) . . . 13_554 ?
O3 Si O1 NaC -56.37(7) 21 . . 13_554 ?
NaB Si O1 NaC 0.000(0) 14_554 . . 13_554 ?
OB Si O1 NaC 0.000(0) 14_554 . . 13_554 ?
OB Si O1 NaC -117.22(6) . . . 13_554 ?
NaB Si O1 NaC 117.22(6) 3 . . 13_554 ?
OB Si O1 NaC 117.22(6) 3 . . 13_554 ?
NaA Si O1 NaC 70.67(9) 15_554 . . 13_554 ?
NaA Si O1 NaC -70.68(9) 14_554 . . 13_554 ?
O2 Si O1 O3 123.63(7) . . . . ?
O3 Si O1 O3 -112.75(14) 21 . . . ?
NaB Si O1 O3 -56.37(7) 14_554 . . . ?
OB Si O1 O3 -56.37(7) 14_554 . . . ?
OB Si O1 O3 -173.59(12) . . . . ?
NaB Si O1 O3 60.84(6) 3 . . . ?
OB Si O1 O3 60.84(6) 3 . . . ?
NaA Si O1 O3 14.30(13) 15_554 . . . ?
NaA Si O1 O3 -127.05(9) 14_554 . . . ?
O2 Si O1 O3 -123.63(7) . . . 21 ?
O3 Si O1 O3 112.75(14) . . . 21 ?
NaB Si O1 O3 56.38(7) 14_554 . . 21 ?
OB Si O1 O3 56.38(7) 14_554 . . 21 ?
OB Si O1 O3 -60.84(6) . . . 21 ?
NaB Si O1 O3 173.59(12) 3 . . 21 ?
OB Si O1 O3 173.59(12) 3 . . 21 ?
NaA Si O1 O3 127.05(9) 15_554 . . 21 ?
NaA Si O1 O3 -14.30(13) 14_554 . . 21 ?
O3 Si O1 O2 -123.63(7) . . . . ?
O3 Si O1 O2 123.63(7) 21 . . . ?
NaB Si O1 O2 180.001(0) 14_554 . . . ?
OB Si O1 O2 180.001(0) 14_554 . . . ?
OB Si O1 O2 62.78(6) . . . . ?
NaB Si O1 O2 -62.78(6) 3 . . . ?
OB Si O1 O2 -62.78(6) 3 . . . ?
NaA Si O1 O2 -109.33(9) 15_554 . . . ?
NaA Si O1 O2 109.33(9) 14_554 . . . ?
O2 Si O1 MnA 109.33(9) . . . 15_554 ?
O3 Si O1 MnA -14.30(13) . . . 15_554 ?
O3 Si O1 MnA -127.05(9) 21 . . 15_554 ?
NaB Si O1 MnA -70.67(9) 14_554 . . 15_554 ?
OB Si O1 MnA -70.67(9) 14_554 . . 15_554 ?
OB Si O1 MnA 172.11(5) . . . 15_554 ?
NaB Si O1 MnA 46.54(15) 3 . . 15_554 ?
OB Si O1 MnA 46.54(15) 3 . . 15_554 ?
NaA Si O1 MnA 0.0 15_554 . . 15_554 ?
NaA Si O1 MnA -141.35(17) 14_554 . . 15_554 ?
O2 Si O1 NaA 109.33(9) . . . 15_554 ?
O3 Si O1 NaA -14.30(13) . . . 15_554 ?
O3 Si O1 NaA -127.05(9) 21 . . 15_554 ?
NaB Si O1 NaA -70.67(9) 14_554 . . 15_554 ?
OB Si O1 NaA -70.67(9) 14_554 . . 15_554 ?
OB Si O1 NaA 172.11(5) . . . 15_554 ?
NaB Si O1 NaA 46.54(15) 3 . . 15_554 ?
OB Si O1 NaA 46.54(15) 3 . . 15_554 ?
NaA Si O1 NaA -141.35(17) 14_554 . . 15_554 ?
O2 Si O1 MnA -109.33(9) . . . 14_554 ?
O3 Si O1 MnA 127.05(9) . . . 14_554 ?
O3 Si O1 MnA 14.30(13) 21 . . 14_554 ?
NaB Si O1 MnA 70.68(9) 14_554 . . 14_554 ?
OB Si O1 MnA 70.68(9) 14_554 . . 14_554 ?
OB Si O1 MnA -46.54(15) . . . 14_554 ?
NaB Si O1 MnA -172.11(5) 3 . . 14_554 ?
OB Si O1 MnA -172.11(5) 3 . . 14_554 ?
NaA Si O1 MnA 141.35(17) 15_554 . . 14_554 ?
NaA Si O1 MnA 0.0 14_554 . . 14_554 ?
O2 Si O1 NaA -109.33(9) . . . 14_554 ?
O3 Si O1 NaA 127.05(9) . . . 14_554 ?
O3 Si O1 NaA 14.30(13) 21 . . 14_554 ?
NaB Si O1 NaA 70.68(9) 14_554 . . 14_554 ?
OB Si O1 NaA 70.68(9) 14_554 . . 14_554 ?
OB Si O1 NaA -46.54(15) . . . 14_554 ?
NaB Si O1 NaA -172.11(5) 3 . . 14_554 ?
OB Si O1 NaA -172.11(5) 3 . . 14_554 ?
NaA Si O1 NaA 141.35(17) 15_554 . . 14_554 ?
O2 Si O1 O1 91.4(3) . . . 2_665 ?
O3 Si O1 O1 -32.3(3) . . . 2_665 ?
O3 Si O1 O1 -145.0(2) 21 . . 2_665 ?
NaB Si O1 O1 -88.6(3) 14_554 . . 2_665 ?
OB Si O1 O1 -88.6(3) 14_554 . . 2_665 ?
OB Si O1 O1 154.1(2) . . . 2_665 ?
NaB Si O1 O1 28.6(3) 3 . . 2_665 ?
OB Si O1 O1 28.6(3) 3 . . 2_665 ?
NaA Si O1 O1 -17.97(17) 15_554 . . 2_665 ?
NaA Si O1 O1 -159.3(3) 14_554 . . 2_665 ?
O2 Si O1 O1 -91.4(3) . . . 3_565 ?
O3 Si O1 O1 145.0(2) . . . 3_565 ?
O3 Si O1 O1 32.3(3) 21 . . 3_565 ?
NaB Si O1 O1 88.6(3) 14_554 . . 3_565 ?
OB Si O1 O1 88.6(3) 14_554 . . 3_565 ?
OB Si O1 O1 -28.6(3) . . . 3_565 ?
NaB Si O1 O1 -154.1(2) 3 . . 3_565 ?
OB Si O1 O1 -154.1(2) 3 . . 3_565 ?
NaA Si O1 O1 159.3(3) 15_554 . . 3_565 ?
NaA Si O1 O1 17.97(17) 14_554 . . 3_565 ?
O1 Si O2 NaC 180.000(1) . . . . ?
O3 Si O2 NaC -59.96(16) . . . . ?
O3 Si O2 NaC 59.96(16) 21 . . . ?
NaB Si O2 NaC -0.004(1) 14_554 . . . ?
OB Si O2 NaC -0.004(1) 14_554 . . . ?
OB Si O2 NaC 79.23(10) . . . . ?
NaB Si O2 NaC -79.22(10) 3 . . . ?
OB Si O2 NaC -79.22(10) 3 . . . ?
NaA Si O2 NaC -114.95(9) 15_554 . . . ?
NaA Si O2 NaC 114.95(9) 14_554 . . . ?
O1 Si O2 NaA 0.000(0) . . . . ?
O3 Si O2 NaA 120.04(16) . . . . ?
O3 Si O2 NaA -120.04(16) 21 . . . ?
NaB Si O2 NaA 179.996(1) 14_554 . . . ?
OB Si O2 NaA 179.996(1) 14_554 . . . ?
OB Si O2 NaA -100.77(10) . . . . ?
NaB Si O2 NaA 100.78(10) 3 . . . ?
OB Si O2 NaA 100.78(10) 3 . . . ?
NaA Si O2 NaA 65.05(9) 15_554 . . . ?
NaA Si O2 NaA -65.05(9) 14_554 . . . ?
O1 Si O2 OB 100.77(10) . . . . ?
O3 Si O2 OB -139.19(15) . . . . ?
O3 Si O2 OB -19.3(2) 21 . . . ?
NaB Si O2 OB -79.23(10) 14_554 . . . ?
OB Si O2 OB -79.23(10) 14_554 . . . ?
NaB Si O2 OB -158.5(2) 3 . . . ?
OB Si O2 OB -158.5(2) 3 . . . ?
NaA Si O2 OB 165.83(4) 15_554 . . . ?
NaA Si O2 OB 35.72(19) 14_554 . . . ?
O1 Si O2 NaB -100.78(10) . . . 3 ?
O3 Si O2 NaB 19.3(2) . . . 3 ?
O3 Si O2 NaB 139.19(15) 21 . . 3 ?
NaB Si O2 NaB 79.22(10) 14_554 . . 3 ?
OB Si O2 NaB 79.22(10) 14_554 . . 3 ?
OB Si O2 NaB 158.5(2) . . . 3 ?
OB Si O2 NaB 0.000(0) 3 . . 3 ?
NaA Si O2 NaB -35.72(19) 15_554 . . 3 ?
NaA Si O2 NaB -165.83(4) 14_554 . . 3 ?
O1 Si O2 OB -100.78(10) . . . 3 ?
O3 Si O2 OB 19.3(2) . . . 3 ?
O3 Si O2 OB 139.19(15) 21 . . 3 ?
NaB Si O2 OB 79.22(10) 14_554 . . 3 ?
OB Si O2 OB 79.22(10) 14_554 . . 3 ?
OB Si O2 OB 158.5(2) . . . 3 ?
NaB Si O2 OB 0.000(0) 3 . . 3 ?
NaA Si O2 OB -35.72(19) 15_554 . . 3 ?
NaA Si O2 OB -165.83(4) 14_554 . . 3 ?
O1 Si O2 O3 120.04(16) . . . 21 ?
O3 Si O2 O3 -119.9(3) . . . 21 ?
NaB Si O2 O3 -59.97(16) 14_554 . . 21 ?
OB Si O2 O3 -59.97(16) 14_554 . . 21 ?
OB Si O2 O3 19.3(2) . . . 21 ?
NaB Si O2 O3 -139.19(15) 3 . . 21 ?
OB Si O2 O3 -139.19(15) 3 . . 21 ?
NaA Si O2 O3 -174.9(2) 15_554 . . 21 ?
NaA Si O2 O3 54.99(14) 14_554 . . 21 ?
O1 Si O2 O3 -120.04(16) . . . . ?
O3 Si O2 O3 119.9(3) 21 . . . ?
NaB Si O2 O3 59.96(16) 14_554 . . . ?
OB Si O2 O3 59.96(16) 14_554 . . . ?
OB Si O2 O3 139.19(15) . . . . ?
NaB Si O2 O3 -19.3(2) 3 . . . ?
OB Si O2 O3 -19.3(2) 3 . . . ?
NaA Si O2 O3 -54.99(14) 15_554 . . . ?
NaA Si O2 O3 174.9(2) 14_554 . . . ?
O3 Si O2 O1 120.04(16) . . . . ?
O3 Si O2 O1 -120.04(16) 21 . . . ?
NaB Si O2 O1 179.996(1) 14_554 . . . ?
OB Si O2 O1 179.996(1) 14_554 . . . ?
OB Si O2 O1 -100.77(11) . . . . ?
NaB Si O2 O1 100.78(10) 3 . . . ?
OB Si O2 O1 100.78(10) 3 . . . ?
NaA Si O2 O1 65.05(9) 15_554 . . . ?
NaA Si O2 O1 -65.05(9) 14_554 . . . ?
O1 Si O2 O3 -54.28(14) . . . 8 ?
O3 Si O2 O3 65.8(2) . . . 8 ?
O3 Si O2 O3 -174.3(2) 21 . . 8 ?
NaB Si O2 O3 125.72(14) 14_554 . . 8 ?
OB Si O2 O3 125.72(14) 14_554 . . 8 ?
OB Si O2 O3 -155.1(2) . . . 8 ?
NaB Si O2 O3 46.50(5) 3 . . 8 ?
OB Si O2 O3 46.50(5) 3 . . 8 ?
NaA Si O2 O3 10.8(2) 15_554 . . 8 ?
NaA Si O2 O3 -119.33(7) 14_554 . . 8 ?
O2 Si O3 Si 69.65(17) . . . 20 ?
O1 Si O3 Si -164.24(13) . . . 20 ?
O3 Si O3 Si -52.96(16) 21 . . 20 ?
NaB Si O3 Si -89.10(8) 14_554 . . 20 ?
OB Si O3 Si -89.10(8) 14_554 . . 20 ?
OB Si O3 Si 6.04(7) . . . 20 ?
NaB Si O3 Si 88.73(9) 3 . . 20 ?
OB Si O3 Si 88.73(9) 3 . . 20 ?
NaA Si O3 Si 180.000(0) 15_554 . . 20 ?
NaA Si O3 Si -104.62(12) 14_554 . . 20 ?
O2 Si O3 MnA -110.35(17) . . . 15_554 ?
O1 Si O3 MnA 15.76(13) . . . 15_554 ?
O3 Si O3 MnA 127.04(16) 21 . . 15_554 ?
NaB Si O3 MnA 90.90(8) 14_554 . . 15_554 ?
OB Si O3 MnA 90.90(8) 14_554 . . 15_554 ?
OB Si O3 MnA -173.96(7) . . . 15_554 ?
NaB Si O3 MnA -91.27(9) 3 . . 15_554 ?
OB Si O3 MnA -91.27(9) 3 . . 15_554 ?
NaA Si O3 MnA 0.0 15_554 . . 15_554 ?
NaA Si O3 MnA 75.38(12) 14_554 . . 15_554 ?
O2 Si O3 NaA -110.35(17) . . . 15_554 ?
O1 Si O3 NaA 15.76(13) . . . 15_554 ?
O3 Si O3 NaA 127.04(16) 21 . . 15_554 ?
NaB Si O3 NaA 90.90(8) 14_554 . . 15_554 ?
OB Si O3 NaA 90.90(8) 14_554 . . 15_554 ?
OB Si O3 NaA -173.96(7) . . . 15_554 ?
NaB Si O3 NaA -91.27(9) 3 . . 15_554 ?
OB Si O3 NaA -91.27(9) 3 . . 15_554 ?
NaA Si O3 NaA 75.38(12) 14_554 . . 15_554 ?
O2 Si O3 O1 -126.1(2) . . . . ?
O3 Si O3 O1 111.3(2) 21 . . . ?
NaB Si O3 O1 75.14(16) 14_554 . . . ?
OB Si O3 O1 75.14(16) 14_554 . . . ?
OB Si O3 O1 170.27(17) . . . . ?
NaB Si O3 O1 -107.03(15) 3 . . . ?
OB Si O3 O1 -107.03(15) 3 . . . ?
NaA Si O3 O1 -15.76(13) 15_554 . . . ?
NaA Si O3 O1 59.61(17) 14_554 . . . ?
O2 Si O3 O1 -77.6(5) . . . 20 ?
O1 Si O3 O1 48.5(5) . . . 20 ?
O3 Si O3 O1 159.8(3) 21 . . 20 ?
NaB Si O3 O1 123.7(5) 14_554 . . 20 ?
OB Si O3 O1 123.7(5) 14_554 . . 20 ?
OB Si O3 O1 -141.2(5) . . . 20 ?
NaB Si O3 O1 -58.5(4) 3 . . 20 ?
OB Si O3 O1 -58.5(4) 3 . . 20 ?
NaA Si O3 O1 32.8(4) 15_554 . . 20 ?
NaA Si O3 O1 108.2(4) 14_554 . . 20 ?
O2 Si O3 O3 122.6(3) . . . 21 ?
O1 Si O3 O3 -111.3(2) . . . 21 ?
NaB Si O3 O3 -36.1(2) 14_554 . . 21 ?
OB Si O3 O3 -36.1(2) 14_554 . . 21 ?
OB Si O3 O3 59.00(18) . . . 21 ?
NaB Si O3 O3 141.70(9) 3 . . 21 ?
OB Si O3 O3 141.70(9) 3 . . 21 ?
NaA Si O3 O3 -127.04(16) 15_554 . . 21 ?
NaA Si O3 O3 -51.66(6) 14_554 . . 21 ?
O2 Si O3 O3 32.4(2) . . . 20 ?
O1 Si O3 O3 158.56(14) . . . 20 ?
O3 Si O3 O3 -90.16(11) 21 . . 20 ?
NaB Si O3 O3 -126.30(15) 14_554 . . 20 ?
OB Si O3 O3 -126.30(15) 14_554 . . 20 ?
OB Si O3 O3 -31.16(13) . . . 20 ?
NaB Si O3 O3 51.53(3) 3 . . 20 ?
OB Si O3 O3 51.53(3) 3 . . 20 ?
NaA Si O3 O3 142.80(7) 15_554 . . 20 ?
NaA Si O3 O3 -141.83(6) 14_554 . . 20 ?
O2 Si O3 NaB -19.1(2) . . . 3 ?
O1 Si O3 NaB 107.03(15) . . . 3 ?
O3 Si O3 NaB -141.70(9) 21 . . 3 ?
NaB Si O3 NaB -177.83(17) 14_554 . . 3 ?
OB Si O3 NaB -177.83(17) 14_554 . . 3 ?
OB Si O3 NaB -82.70(13) . . . 3 ?
OB Si O3 NaB 0.000(0) 3 . . 3 ?
NaA Si O3 NaB 91.27(9) 15_554 . . 3 ?
NaA Si O3 NaB 166.64(6) 14_554 . . 3 ?
O2 Si O3 OB -19.1(2) . . . 3 ?
O1 Si O3 OB 107.03(15) . . . 3 ?
O3 Si O3 OB -141.70(9) 21 . . 3 ?
NaB Si O3 OB -177.83(17) 14_554 . . 3 ?
OB Si O3 OB -177.83(17) 14_554 . . 3 ?
OB Si O3 OB -82.70(13) . . . 3 ?
NaB Si O3 OB 0.000(0) 3 . . 3 ?
NaA Si O3 OB 91.27(9) 15_554 . . 3 ?
NaA Si O3 OB 166.64(6) 14_554 . . 3 ?
O2 Si O3 NaB 158.75(17) . . . 14_554 ?
O1 Si O3 NaB -75.14(16) . . . 14_554 ?
O3 Si O3 NaB 36.1(2) 21 . . 14_554 ?
OB Si O3 NaB 0.0 14_554 . . 14_554 ?
OB Si O3 NaB 95.13(10) . . . 14_554 ?
NaB Si O3 NaB 177.83(17) 3 . . 14_554 ?
OB Si O3 NaB 177.83(17) 3 . . 14_554 ?
NaA Si O3 NaB -90.90(8) 15_554 . . 14_554 ?
NaA Si O3 NaB -15.5(2) 14_554 . . 14_554 ?
O2 Si O3 OB 158.75(17) . . . 14_554 ?
O1 Si O3 OB -75.14(16) . . . 14_554 ?
O3 Si O3 OB 36.1(2) 21 . . 14_554 ?
NaB Si O3 OB 0.0 14_554 . . 14_554 ?
OB Si O3 OB 95.13(10) . . . 14_554 ?
NaB Si O3 OB 177.83(17) 3 . . 14_554 ?
OB Si O3 OB 177.83(17) 3 . . 14_554 ?
NaA Si O3 OB -90.90(8) 15_554 . . 14_554 ?
NaA Si O3 OB -15.5(2) 14_554 . . 14_554 ?
 
_refine_diff_density_max    1.285
_refine_diff_density_min   -0.779
_refine_diff_density_rms    0.183