data_pseudomarkeyite
 
_audit_creation_method            'SHELXL-2016/6'
_shelx_SHELXL_version_number      '2016/6'
_chemical_name_mineral            'pseudomarkeyite' 
_chemical_compound_source         'Markey mine, Utah'
_chemical_formula_sum
 'C12 H42 Ca8 O65 U4' 
_chemical_formula_weight          2499.21

loop_
 _atom_type_symbol
 _atom_type_description
 _atom_type_scat_dispersion_real
 _atom_type_scat_dispersion_imag
 _atom_type_scat_source
 'C'  'C'   0.0033   0.0016
 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4'
 'H'  'H'   0.0000   0.0000
 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4'
 'Ca'  'Ca'   0.2262   0.3064
 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4'
 'O'  'O'   0.0106   0.0060
 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4'
 'U'  'U'  -9.6767   9.6646
 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4'
 
_space_group_crystal_system       monoclinic
_space_group_IT_number            11
_space_group_name_H-M_alt         'P 21/m'
_space_group_name_Hall            '-P 2yb'
 
_shelx_space_group_comment
;
The symmetry employed for this shelxl refinement is uniquely defined
by the following loop, which should always be used as a source of
symmetry information in preference to the above space-group names.
They are only intended as comments.
;
 
loop_
 _space_group_symop_operation_xyz
 'x, y, z'
 '-x, y+1/2, -z'
 '-x, -y, -z'
 'x, -y-1/2, z'
 
_cell_length_a                    17.531(3)
_cell_length_b                    18.555(3)
_cell_length_c                    9.130(3)
_cell_angle_alpha                 90
_cell_angle_beta                  103.95(3)
_cell_angle_gamma                 90
_cell_volume                      2882.3(13)
_cell_formula_units_Z             2
_cell_measurement_temperature     293(2)
_cell_measurement_reflns_used     6958
_cell_measurement_theta_min       3.0
_cell_measurement_theta_max       19.9
_exptl_crystal_density_diffrn     2.880          
_exptl_crystal_F_000              2324
_exptl_crystal_size_max           0.120
_exptl_crystal_size_mid           0.070
_exptl_crystal_size_min           0.030
_exptl_absorpt_coefficient_mu     12.059
_exptl_absorpt_correction_type    multi-scan 
_exptl_absorpt_process_details    Higashi2001 
_exptl_absorpt_correction_T_max   1.000
_exptl_absorpt_correction_T_min   0.069
_exptl_crystal_description        'Chunk'
_exptl_crystal_colour             'Yellow'
_shelx_estimated_absorpt_T_min    0.326
_shelx_estimated_absorpt_T_max    0.714
_diffrn_measurement_device_type   'Rigaku R-axis RAPID II'
_diffrn_ambient_temperature       293(2)
_diffrn_radiation_wavelength      0.71075
_diffrn_radiation_type            MoK\a
_diffrn_source                    'fine-focus sealed tube'                       
_diffrn_radiation_monochromator   graphite 
_diffrn_reflns_number             11253
_diffrn_reflns_av_unetI/netI      0.0938
_diffrn_reflns_av_R_equivalents   0.1174
_diffrn_reflns_limit_h_min        -16
_diffrn_reflns_limit_h_max        16
_diffrn_reflns_limit_k_min        -17
_diffrn_reflns_limit_k_max        16
_diffrn_reflns_limit_l_min        -8
_diffrn_reflns_limit_l_max        8
_diffrn_reflns_theta_min          3.042
_diffrn_reflns_theta_max          19.959
_diffrn_reflns_theta_full         19.959
_diffrn_measured_fraction_theta_max   0.995
_diffrn_measured_fraction_theta_full  0.995
_diffrn_reflns_Laue_measured_fraction_max    0.995
_diffrn_reflns_Laue_measured_fraction_full   0.995
_diffrn_reflns_point_group_measured_fraction_max   0.995
_diffrn_reflns_point_group_measured_fraction_full  0.995
_reflns_number_total              2772
_reflns_number_gt                 2106
_reflns_threshold_expression      'I > 2σ(I)'
_reflns_Friedel_coverage          0.000
_reflns_Friedel_fraction_max      .
_reflns_Friedel_fraction_full     .
 
_reflns_special_details
;
 Reflections were merged by SHELXL according to the crystal
 class for the calculation of statistics and refinement.
 
 _reflns_Friedel_fraction is defined as the number of unique
 Friedel pairs measured divided by the number that would be
 possible theoretically, ignoring centric projections and
 systematic absences.
;
 
_computing_data_collection        ?
_computing_cell_refinement        ?
_computing_data_reduction         ?
_computing_structure_solution     ?
_computing_structure_refinement 'SHELXL-2016/6 (Sheldrick, 2016)'
_computing_molecular_graphics     ?
_computing_publication_material   ?
_refine_special_details           ?
_refine_ls_structure_factor_coef  Fsqd
_refine_ls_matrix_type            full
_refine_ls_weighting_scheme       calc
_refine_ls_weighting_details
'w=1/[σ²(Fo²)+(0.1226P)²+100.5513P] where P=(Fo²+2Fc²)/3'
_atom_sites_solution_primary      ?
_atom_sites_solution_secondary    ?
_atom_sites_solution_hydrogens    .
_refine_ls_hydrogen_treatment     undef
_refine_ls_extinction_method      none
_refine_ls_extinction_coef        .
_refine_ls_number_reflns          2772
_refine_ls_number_parameters      226
_refine_ls_number_restraints      0
_refine_ls_R_factor_all           0.1023
_refine_ls_R_factor_gt            0.0787
_refine_ls_wR_factor_ref          0.2267
_refine_ls_wR_factor_gt           0.2015
_refine_ls_goodness_of_fit_ref    1.055
_refine_ls_restrained_S_all       1.055
_refine_ls_shift/su_max           0.000
_refine_ls_shift/su_mean          0.000
 
loop_
 _atom_site_label
 _atom_site_type_symbol
 _atom_site_fract_x
 _atom_site_fract_y
 _atom_site_fract_z
 _atom_site_U_iso_or_equiv
 _atom_site_adp_type
 _atom_site_occupancy
 _atom_site_site_symmetry_order  
 _atom_site_calc_flag
 _atom_site_refinement_flags_posn
 _atom_site_refinement_flags_adp
 _atom_site_refinement_flags_occupancy
 _atom_site_disorder_assembly
 _atom_site_disorder_group
Ca1 Ca 0.3218(4) 0.4523(4) 0.3212(7) 0.0446(18) Uani 1 1 d . . . . .
Ca2 Ca 0.0353(3) 0.5605(3) 0.6980(8) 0.0419(17) Uani 1 1 d . . . . .
Ca3 Ca 0.1455(5) 0.250000 0.9299(11) 0.050(3) Uani 1 2 d S T P . .
Ca4 Ca 0.1983(5) 0.750000 0.0965(11) 0.046(3) Uani 1 2 d S T P . .
Ca5 Ca 0.4234(3) 0.5655(3) 0.0674(7) 0.0371(16) Uani 1 1 d . . . . .
U1 U 0.25997(7) 0.53908(7) 0.67504(14) 0.0418(5) Uani 1 1 d . . . . .
U2 U 0.52292(10) 0.750000 0.9815(2) 0.0408(6) Uani 1 2 d S T P . .
U3 U 0.97059(10) 0.750000 0.4935(2) 0.0457(6) Uani 1 2 d S T P . .
C1 C 0.2212(19) 0.5975(17) 0.937(4) 0.046(9) Uiso 1 1 d . . . . .
C2 C 0.4169(19) 0.4919(17) 0.697(4) 0.047(9) Uiso 1 1 d . . . . .
C3 C 0.1409(17) 0.5037(16) 0.410(4) 0.040(8) Uiso 1 1 d . . . . .
C4 C 0.4163(16) 0.3845(15) 0.086(3) 0.034(8) Uiso 1 1 d . . . . .
C5 C 0.389(3) 0.750000 0.125(6) 0.075(17) Uiso 1 2 d S . P . .
C6 C 0.051(2) 0.3833(19) 0.666(4) 0.059(10) Uiso 1 1 d . . . . .
C7 C 0.045(2) 0.750000 0.817(5) 0.039(11) Uiso 1 2 d S . P . .
O1 O 0.1690(11) 0.5831(10) 0.817(2) 0.040(5) Uiso 1 1 d . . . . .
O2 O 0.2906(12) 0.5777(11) 0.938(2) 0.049(6) Uiso 1 1 d . . . . .
O3 O 0.2045(11) 0.6246(11) 0.053(2) 0.042(5) Uiso 1 1 d . . . . .
O4 O 0.4789(12) 0.4585(10) 0.702(2) 0.044(6) Uiso 1 1 d . . . . .
O5 O 0.3649(11) 0.4992(10) 0.573(2) 0.042(5) Uiso 1 1 d . . . . .
O6 O 0.3991(10) 0.5254(10) 0.811(2) 0.033(5) Uiso 1 1 d . . . . .
O7 O 0.9072(14) 0.5221(13) 0.698(3) 0.064(7) Uiso 1 1 d . . . . .
O8 O 0.1235(10) 0.5321(9) 0.526(2) 0.033(5) Uiso 1 1 d . . . . .
O9 O 0.2172(12) 0.5065(12) 0.416(2) 0.054(6) Uiso 1 1 d . . . . .
O10 O 0.3868(12) 0.3258(12) 0.115(2) 0.053(6) Uiso 1 1 d . . . . .
O11 O 0.4708(11) 0.3827(11) 0.022(2) 0.041(5) Uiso 1 1 d . . . . .
O12 O 0.3884(12) 0.4457(11) 0.119(2) 0.045(6) Uiso 1 1 d . . . . .
O13 O 0.3325(17) 0.750000 0.176(3) 0.047(8) Uiso 1 2 d S . P . .
O14 O 0.4260(11) 0.6917(10) 0.096(2) 0.037(5) Uiso 1 1 d . . . . .
O15 O 0.9694(13) 0.6192(12) 0.473(3) 0.058(6) Uiso 1 1 d . . . . .
O16 O 0.0725(14) 0.3209(13) 0.734(3) 0.071(7) Uiso 1 1 d . . . . .
O17 O 0.0599(13) 0.4400(12) 0.754(3) 0.058(6) Uiso 1 1 d . . . . .
O18 O 0.0744(16) 0.750000 0.948(3) 0.044(8) Uiso 1 2 d S . P . .
O19 O 0.0213(13) 0.8074(12) 0.736(2) 0.057(6) Uiso 1 1 d . . . . .
O20 O 0.2755(11) 0.6294(10) 0.629(2) 0.042(5) Uiso 1 1 d . . . . .
O21 O 0.2454(12) 0.4476(12) 0.724(2) 0.055(6) Uiso 1 1 d . . . . .
O22 O 0.4555(17) 0.750000 0.804(3) 0.051(8) Uiso 1 2 d S . P . .
O23 O 0.5971(16) 0.750000 0.161(3) 0.044(8) Uiso 1 2 d S . P . .
O24 O 0.0633(17) 0.750000 0.460(3) 0.053(8) Uiso 1 2 d S . P . .
O25 O 0.8754(19) 0.750000 0.529(4) 0.065(10) Uiso 1 2 d S . P . .
OW1 O 0.4398(13) 0.3822(13) 0.444(3) 0.067(7) Uiso 1 1 d . . . . .
OW2 O 0.164(2) 0.6743(19) 0.301(4) 0.120(11) Uiso 1 1 d . . . . .
OW3 O 0.2101(14) 0.4536(13) 0.111(3) 0.067(7) Uiso 1 1 d . . . . .
OW4 O 0.2290(19) 0.750000 0.827(4) 0.069(10) Uiso 1 2 d S . P . .
OW5 O 0.3429(11) 0.5777(10) 0.260(2) 0.042(5) Uiso 1 1 d . . . . .
OW6 O 0.0427(13) 0.5698(13) 0.983(3) 0.064(7) Uiso 1 1 d . . . . .
OW7 O 0.2580(17) 0.3498(16) 0.408(3) 0.094(9) Uiso 1 1 d . . . . .
OW8 O 0.251(2) 0.250000 0.162(5) 0.096(13) Uiso 1 2 d S . P . .
OW9 O 0.243(2) 0.167(2) 0.904(5) 0.150(14) Uiso 1 1 d . . . . .
OW10 O 0.0902(19) 0.1658(17) 0.073(4) 0.109(10) Uiso 1 1 d . . . . .
OW11 O 0.4046(12) 0.6725(11) 0.496(2) 0.047(6) Uiso 1 1 d . . . . .
OW12 O 0.390(3) 0.250000 0.534(5) 0.104(14) Uiso 1 2 d S . P . .
 
 
_geom_special_details
;
 All esds (except the esd in the dihedral angle between two l.s. planes)
 are estimated using the full covariance matrix.  The cell esds are taken
 into account individually in the estimation of esds in distances, angles
 and torsion angles; correlations between esds in cell parameters are only
 used when they are defined by crystal symmetry.  An approximate (isotropic)
 treatment of cell esds is used for estimating esds involving l.s. planes.
;
 
loop_
 _geom_bond_atom_site_label_1
 _geom_bond_atom_site_label_2
 _geom_bond_distance
 _geom_bond_site_symmetry_2
 _geom_bond_publ_flag
Ca1 OW3 2.39(2) . ?
Ca1 O5 2.40(2) . ?
Ca1 O12 2.41(2) . ?
Ca1 O9 2.42(2) . ?
Ca1 OW7 2.43(3) . ?
Ca1 OW5 2.44(2) . ?
Ca1 OW1 2.47(2) . ?
Ca1 Ca5 3.866(9) . ?
Ca1 U1 3.987(7) . ?
Ca2 O17 2.31(2) . ?
Ca2 O7 2.36(2) 1_455 ?
Ca2 O15 2.36(2) 1_455 ?
Ca2 O1 2.37(2) . ?
Ca2 O19 2.50(2) 4_575 ?
Ca2 O8 2.509(19) . ?
Ca2 OW6 2.58(2) . ?
Ca2 C3 3.24(3) 3_566 ?
Ca2 U1 4.014(6) . ?
Ca2 U3 4.015(6) 1_455 ?
Ca2 Ca2 4.182(13) 3_566 ?
Ca3 O16 2.34(3) . ?
Ca3 O16 2.34(3) 4_565 ?
Ca3 OW9 2.35(4) . ?
Ca3 OW9 2.35(4) 4_565 ?
Ca3 OW10 2.39(3) 4_566 ?
Ca3 OW10 2.39(3) 1_556 ?
Ca3 OW8 2.46(4) 1_556 ?
Ca3 U3 3.910(10) 3_666 ?
Ca4 O18 2.27(3) 1_554 ?
Ca4 O13 2.29(3) . ?
Ca4 O3 2.37(2) 4_575 ?
Ca4 O3 2.37(2) . ?
Ca4 OW2 2.52(3) . ?
Ca4 OW2 2.52(3) 4_575 ?
Ca4 OW4 2.64(4) 1_554 ?
Ca4 C7 3.24(4) 1_554 ?
Ca5 O2 2.35(2) 1_554 ?
Ca5 O14 2.354(19) . ?
Ca5 O12 2.38(2) . ?
Ca5 O6 2.39(2) 1_554 ?
Ca5 O11 2.40(2) 3_665 ?
Ca5 O4 2.41(2) 3_666 ?
Ca5 OW5 2.51(2) . ?
Ca5 U2 4.004(6) 1_554 ?
Ca5 Ca5 4.029(12) 3_665 ?
Ca5 U1 4.041(6) 1_554 ?
U1 O20 1.765(19) . ?
U1 O21 1.79(2) . ?
U1 O5 2.372(19) . ?
U1 O9 2.38(2) . ?
U1 O1 2.425(19) . ?
U1 O2 2.43(2) . ?
U1 O8 2.454(18) . ?
U1 O6 2.469(18) . ?
U1 C2 2.85(3) . ?
U1 C1 2.85(3) . ?
U1 C3 2.87(3) . ?
U2 O22 1.76(3) . ?
U2 O23 1.83(3) 1_556 ?
U2 O10 2.43(2) 2_656 ?
U2 O10 2.43(2) 3_666 ?
U2 O14 2.452(18) 1_556 ?
U2 O14 2.452(18) 4_576 ?
U2 O11 2.47(2) 2_656 ?
U2 O11 2.47(2) 3_666 ?
U2 C4 2.84(3) 2_656 ?
U2 C4 2.84(3) 3_666 ?
U2 C5 2.96(6) 1_556 ?
U3 O24 1.72(3) 1_655 ?
U3 O25 1.78(3) . ?
U3 O16 2.42(2) 3_666 ?
U3 O16 2.42(2) 2_656 ?
U3 O19 2.42(2) 1_655 ?
U3 O19 2.42(2) 4_675 ?
U3 O15 2.43(2) 4_575 ?
U3 O15 2.43(2) . ?
U3 C6 2.85(4) 3_666 ?
U3 C6 2.85(4) 2_656 ?
U3 C7 2.92(4) 1_655 ?
C1 O3 1.27(3) 1_556 ?
C1 O2 1.27(3) . ?
C1 O1 1.28(3) . ?
C2 O4 1.24(3) . ?
C2 O5 1.28(3) . ?
C2 O6 1.32(3) . ?
C3 O7 1.23(3) 3_666 ?
C3 O8 1.29(3) . ?
C3 O9 1.33(3) . ?
C4 O11 1.23(3) . ?
C4 O10 1.26(3) . ?
C4 O12 1.30(3) . ?
C5 O13 1.19(6) . ?
C5 O14 1.32(4) 4_575 ?
C5 O14 1.32(4) . ?
C6 O15 1.23(4) 3_666 ?
C6 O17 1.31(4) . ?
C6 O16 1.32(4) . ?
C7 O18 1.18(4) . ?
C7 O19 1.30(3) 4_575 ?
C7 O19 1.30(3) . ?
 
loop_
 _geom_angle_atom_site_label_1
 _geom_angle_atom_site_label_2
 _geom_angle_atom_site_label_3
 _geom_angle
 _geom_angle_site_symmetry_1
 _geom_angle_site_symmetry_3
 _geom_angle_publ_flag
OW3 Ca1 O5 140.6(8) . . ?
OW3 Ca1 O12 80.8(8) . . ?
O5 Ca1 O12 130.7(7) . . ?
OW3 Ca1 O9 74.8(8) . . ?
O5 Ca1 O9 66.4(7) . . ?
O12 Ca1 O9 147.1(8) . . ?
OW3 Ca1 OW7 85.2(9) . . ?
O5 Ca1 OW7 92.0(8) . . ?
O12 Ca1 OW7 123.7(9) . . ?
O9 Ca1 OW7 76.2(9) . . ?
OW3 Ca1 OW5 86.9(8) . . ?
O5 Ca1 OW5 81.1(7) . . ?
O12 Ca1 OW5 75.2(7) . . ?
O9 Ca1 OW5 81.7(7) . . ?
OW7 Ca1 OW5 157.8(9) . . ?
OW3 Ca1 OW1 143.5(8) . . ?
O5 Ca1 OW1 73.8(7) . . ?
O12 Ca1 OW1 79.3(7) . . ?
O9 Ca1 OW1 132.8(8) . . ?
OW7 Ca1 OW1 80.9(9) . . ?
OW5 Ca1 OW1 116.7(7) . . ?
OW3 Ca1 Ca5 85.4(6) . . ?
O5 Ca1 Ca5 107.0(5) . . ?
O12 Ca1 Ca5 36.0(5) . . ?
O9 Ca1 Ca5 119.0(6) . . ?
OW7 Ca1 Ca5 159.1(7) . . ?
OW5 Ca1 Ca5 39.4(5) . . ?
OW1 Ca1 Ca5 95.8(6) . . ?
OW3 Ca1 U1 108.4(6) . . ?
O5 Ca1 U1 33.2(5) . . ?
O12 Ca1 U1 156.4(5) . . ?
O9 Ca1 U1 33.7(5) . . ?
OW7 Ca1 U1 79.4(7) . . ?
OW5 Ca1 U1 83.5(5) . . ?
OW1 Ca1 U1 101.9(6) . . ?
Ca5 Ca1 U1 121.39(19) . . ?
O17 Ca2 O7 80.5(8) . 1_455 ?
O17 Ca2 O15 131.6(8) . 1_455 ?
O7 Ca2 O15 82.8(8) 1_455 1_455 ?
O17 Ca2 O1 87.6(7) . . ?
O7 Ca2 O1 152.9(8) 1_455 . ?
O15 Ca2 O1 122.6(7) 1_455 . ?
O17 Ca2 O19 159.8(8) . 4_575 ?
O7 Ca2 O19 99.8(8) 1_455 4_575 ?
O15 Ca2 O19 67.9(8) 1_455 4_575 ?
O1 Ca2 O19 83.3(7) . 4_575 ?
O17 Ca2 O8 79.9(7) . . ?
O7 Ca2 O8 131.9(8) 1_455 . ?
O15 Ca2 O8 78.5(7) 1_455 . ?
O1 Ca2 O8 68.5(6) . . ?
O19 Ca2 O8 112.9(7) 4_575 . ?
O17 Ca2 OW6 83.1(8) . . ?
O7 Ca2 OW6 80.5(8) 1_455 . ?
O15 Ca2 OW6 137.7(8) 1_455 . ?
O1 Ca2 OW6 73.9(7) . . ?
O19 Ca2 OW6 77.1(7) 4_575 . ?
O8 Ca2 OW6 139.1(7) . . ?
O17 Ca2 C3 79.9(8) . 3_566 ?
O7 Ca2 C3 18.0(8) 1_455 3_566 ?
O15 Ca2 C3 71.0(8) 1_455 3_566 ?
O1 Ca2 C3 166.1(8) . 3_566 ?
O19 Ca2 C3 106.5(8) 4_575 3_566 ?
O8 Ca2 C3 114.8(7) . 3_566 ?
OW6 Ca2 C3 98.3(8) . 3_566 ?
O17 Ca2 U1 77.4(6) . . ?
O7 Ca2 U1 156.6(6) 1_455 . ?
O15 Ca2 U1 106.3(6) 1_455 . ?
O1 Ca2 U1 33.6(5) . . ?
O19 Ca2 U1 103.6(5) 4_575 . ?
O8 Ca2 U1 35.6(4) . . ?
OW6 Ca2 U1 104.4(5) . . ?
C3 Ca2 U1 145.6(6) 3_566 . ?
O17 Ca2 U3 165.3(6) . 1_455 ?
O7 Ca2 U3 95.9(6) 1_455 1_455 ?
O15 Ca2 U3 33.7(6) 1_455 1_455 ?
O1 Ca2 U3 101.3(5) . 1_455 ?
O19 Ca2 U3 34.7(5) 4_575 1_455 ?
O8 Ca2 U3 92.3(4) . 1_455 ?
OW6 Ca2 U3 110.5(6) . 1_455 ?
C3 Ca2 U3 92.2(6) 3_566 1_455 ?
U1 Ca2 U3 103.49(14) . 1_455 ?
O17 Ca2 Ca2 70.9(6) . 3_566 ?
O7 Ca2 Ca2 75.9(6) 1_455 3_566 ?
O15 Ca2 Ca2 61.1(6) 1_455 3_566 ?
O1 Ca2 Ca2 123.0(5) . 3_566 ?
O19 Ca2 Ca2 128.9(6) 4_575 3_566 ?
O8 Ca2 Ca2 56.3(4) . 3_566 ?
OW6 Ca2 Ca2 147.2(6) . 3_566 ?
C3 Ca2 Ca2 58.5(6) 3_566 3_566 ?
U1 Ca2 Ca2 89.5(2) . 3_566 ?
U3 Ca2 Ca2 94.4(2) 1_455 3_566 ?
O16 Ca3 O16 68.5(12) . 4_565 ?
O16 Ca3 OW9 124.6(12) . . ?
O16 Ca3 OW9 80.1(12) 4_565 . ?
O16 Ca3 OW9 80.1(12) . 4_565 ?
O16 Ca3 OW9 124.6(12) 4_565 4_565 ?
OW9 Ca3 OW9 82(2) . 4_565 ?
O16 Ca3 OW10 80.2(10) . 4_566 ?
O16 Ca3 OW10 124.6(10) 4_565 4_566 ?
OW9 Ca3 OW10 152.2(13) . 4_566 ?
OW9 Ca3 OW10 91.3(12) 4_565 4_566 ?
O16 Ca3 OW10 124.6(10) . 1_556 ?
O16 Ca3 OW10 80.2(10) 4_565 1_556 ?
OW9 Ca3 OW10 91.3(12) . 1_556 ?
OW9 Ca3 OW10 152.2(13) 4_565 1_556 ?
OW10 Ca3 OW10 81.8(16) 4_566 1_556 ?
O16 Ca3 OW8 145.1(6) . 1_556 ?
O16 Ca3 OW8 145.1(6) 4_565 1_556 ?
OW9 Ca3 OW8 70.9(12) . 1_556 ?
OW9 Ca3 OW8 70.9(12) 4_565 1_556 ?
OW10 Ca3 OW8 81.4(11) 4_566 1_556 ?
OW10 Ca3 OW8 81.4(11) 1_556 1_556 ?
O16 Ca3 U3 35.4(6) . 3_666 ?
O16 Ca3 U3 35.4(6) 4_565 3_666 ?
OW9 Ca3 U3 96.7(10) . 3_666 ?
OW9 Ca3 U3 96.7(10) 4_565 3_666 ?
OW10 Ca3 U3 110.9(8) 4_566 3_666 ?
OW10 Ca3 U3 110.9(8) 1_556 3_666 ?
OW8 Ca3 U3 163.2(10) 1_556 3_666 ?
O18 Ca4 O13 162.4(11) 1_554 . ?
O18 Ca4 O3 88.6(5) 1_554 4_575 ?
O13 Ca4 O3 88.2(5) . 4_575 ?
O18 Ca4 O3 88.6(5) 1_554 . ?
O13 Ca4 O3 88.2(5) . . ?
O3 Ca4 O3 158.7(11) 4_575 . ?
O18 Ca4 OW2 94.4(10) 1_554 . ?
O13 Ca4 OW2 100.2(10) . . ?
O3 Ca4 OW2 134.5(10) 4_575 . ?
O3 Ca4 OW2 66.8(9) . . ?
O18 Ca4 OW2 94.4(10) 1_554 4_575 ?
O13 Ca4 OW2 100.2(10) . 4_575 ?
O3 Ca4 OW2 66.8(9) 4_575 4_575 ?
O3 Ca4 OW2 134.5(10) . 4_575 ?
OW2 Ca4 OW2 67.7(16) . 4_575 ?
O18 Ca4 OW4 79.8(11) 1_554 1_554 ?
O13 Ca4 OW4 82.6(11) . 1_554 ?
O3 Ca4 OW4 79.4(5) 4_575 1_554 ?
O3 Ca4 OW4 79.4(5) . 1_554 ?
OW2 Ca4 OW4 145.8(8) . 1_554 ?
OW2 Ca4 OW4 145.8(8) 4_575 1_554 ?
O18 Ca4 C7 14.5(10) 1_554 1_554 ?
O13 Ca4 C7 147.9(11) . 1_554 ?
O3 Ca4 C7 86.0(5) 4_575 1_554 ?
O3 Ca4 C7 86.0(5) . 1_554 ?
OW2 Ca4 C7 106.3(10) . 1_554 ?
OW2 Ca4 C7 106.3(10) 4_575 1_554 ?
OW4 Ca4 C7 65.3(11) 1_554 1_554 ?
O2 Ca5 O14 87.2(7) 1_554 . ?
O2 Ca5 O12 85.4(7) 1_554 . ?
O14 Ca5 O12 154.7(7) . . ?
O2 Ca5 O6 67.4(7) 1_554 1_554 ?
O14 Ca5 O6 114.3(7) . 1_554 ?
O12 Ca5 O6 84.8(7) . 1_554 ?
O2 Ca5 O11 122.8(7) 1_554 3_665 ?
O14 Ca5 O11 69.2(7) . 3_665 ?
O12 Ca5 O11 134.2(7) . 3_665 ?
O6 Ca5 O11 76.2(6) 1_554 3_665 ?
O2 Ca5 O4 149.8(8) 1_554 3_666 ?
O14 Ca5 O4 95.5(7) . 3_666 ?
O12 Ca5 O4 79.5(7) . 3_666 ?
O6 Ca5 O4 135.8(7) 1_554 3_666 ?
O11 Ca5 O4 85.8(7) 3_665 3_666 ?
O2 Ca5 OW5 71.9(7) 1_554 . ?
O14 Ca5 OW5 80.3(7) . . ?
O12 Ca5 OW5 74.4(7) . . ?
O6 Ca5 OW5 135.5(7) 1_554 . ?
O11 Ca5 OW5 144.3(7) 3_665 . ?
O4 Ca5 OW5 78.9(7) 3_666 . ?
O2 Ca5 Ca1 79.2(5) 1_554 . ?
O14 Ca5 Ca1 118.2(5) . . ?
O12 Ca5 Ca1 36.6(5) . . ?
O6 Ca5 Ca1 114.7(5) 1_554 . ?
O11 Ca5 Ca1 158.0(5) 3_665 . ?
O4 Ca5 Ca1 73.1(5) 3_666 . ?
OW5 Ca5 Ca1 38.1(5) . . ?
O2 Ca5 U2 104.1(5) 1_554 1_554 ?
O14 Ca5 U2 34.3(5) . 1_554 ?
O12 Ca5 U2 168.8(5) . 1_554 ?
O6 Ca5 U2 93.3(5) 1_554 1_554 ?
O11 Ca5 U2 35.2(5) 3_665 1_554 ?
O4 Ca5 U2 94.5(5) 3_666 1_554 ?
OW5 Ca5 U2 113.8(5) . 1_554 ?
Ca1 Ca5 U2 150.1(2) . 1_554 ?
O2 Ca5 Ca5 123.7(6) 1_554 3_665 ?
O14 Ca5 Ca5 129.6(5) . 3_665 ?
O12 Ca5 Ca5 73.7(5) . 3_665 ?
O6 Ca5 Ca5 59.2(5) 1_554 3_665 ?
O11 Ca5 Ca5 60.7(5) 3_665 3_665 ?
O4 Ca5 Ca5 76.7(5) 3_666 3_665 ?
OW5 Ca5 Ca5 142.7(5) . 3_665 ?
Ca1 Ca5 Ca5 107.0(2) . 3_665 ?
U2 Ca5 Ca5 95.9(2) 1_554 3_665 ?
O2 Ca5 U1 33.1(5) 1_554 1_554 ?
O14 Ca5 U1 102.1(5) . 1_554 ?
O12 Ca5 U1 84.3(5) . 1_554 ?
O6 Ca5 U1 34.4(4) 1_554 1_554 ?
O11 Ca5 U1 100.8(5) 3_665 1_554 ?
O4 Ca5 U1 162.4(5) 3_666 1_554 ?
OW5 Ca5 U1 103.4(5) . 1_554 ?
Ca1 Ca5 U1 97.75(16) . 1_554 ?
U2 Ca5 U1 100.35(14) 1_554 1_554 ?
Ca5 Ca5 U1 92.2(2) 3_665 1_554 ?
O20 U1 O21 179.2(9) . . ?
O20 U1 O5 91.3(8) . . ?
O21 U1 O5 88.6(8) . . ?
O20 U1 O9 91.8(8) . . ?
O21 U1 O9 88.9(9) . . ?
O5 U1 O9 67.6(7) . . ?
O20 U1 O1 88.2(8) . . ?
O21 U1 O1 91.9(8) . . ?
O5 U1 O1 170.7(7) . . ?
O9 U1 O1 121.8(7) . . ?
O20 U1 O2 87.0(8) . . ?
O21 U1 O2 92.4(9) . . ?
O5 U1 O2 118.1(7) . . ?
O9 U1 O2 174.2(7) . . ?
O1 U1 O2 52.6(7) . . ?
O20 U1 O8 95.9(7) . . ?
O21 U1 O8 84.8(8) . . ?
O5 U1 O8 120.8(6) . . ?
O9 U1 O8 53.5(7) . . ?
O1 U1 O8 68.6(6) . . ?
O2 U1 O8 121.0(7) . . ?
O20 U1 O6 91.6(7) . . ?
O21 U1 O6 87.7(8) . . ?
O5 U1 O6 53.1(6) . . ?
O9 U1 O6 120.6(7) . . ?
O1 U1 O6 117.6(6) . . ?
O2 U1 O6 65.0(6) . . ?
O8 U1 O6 170.5(6) . . ?
O20 U1 C2 96.1(9) . . ?
O21 U1 C2 83.4(9) . . ?
O5 U1 C2 26.3(8) . . ?
O9 U1 C2 93.3(8) . . ?
O1 U1 C2 144.5(8) . . ?
O2 U1 C2 92.4(8) . . ?
O8 U1 C2 145.0(8) . . ?
O6 U1 C2 27.5(7) . . ?
O20 U1 C1 85.6(9) . . ?
O21 U1 C1 94.1(9) . . ?
O5 U1 C1 144.2(8) . . ?
O9 U1 C1 148.0(8) . . ?
O1 U1 C1 26.4(7) . . ?
O2 U1 C1 26.3(7) . . ?
O8 U1 C1 95.0(8) . . ?
O6 U1 C1 91.3(8) . . ?
C2 U1 C1 118.6(9) . . ?
O20 U1 C3 97.9(9) . . ?
O21 U1 C3 82.9(9) . . ?
O5 U1 C3 94.2(8) . . ?
O9 U1 C3 27.4(7) . . ?
O1 U1 C3 95.1(8) . . ?
O2 U1 C3 147.4(8) . . ?
O8 U1 C3 26.6(7) . . ?
O6 U1 C3 146.2(8) . . ?
C2 U1 C3 118.9(9) . . ?
C1 U1 C3 121.6(9) . . ?
O20 U1 Ca1 95.8(6) . . ?
O21 U1 Ca1 84.5(7) . . ?
O5 U1 Ca1 33.7(5) . . ?
O9 U1 Ca1 34.3(5) . . ?
O1 U1 Ca1 155.6(5) . . ?
O2 U1 Ca1 151.4(5) . . ?
O8 U1 Ca1 87.1(4) . . ?
O6 U1 Ca1 86.4(4) . . ?
C2 U1 Ca1 59.0(7) . . ?
C1 U1 Ca1 177.4(7) . . ?
C3 U1 Ca1 60.5(6) . . ?
O22 U2 O23 177.0(13) . 1_556 ?
O22 U2 O10 91.1(9) . 2_656 ?
O23 U2 O10 86.4(9) 1_556 2_656 ?
O22 U2 O10 91.1(9) . 3_666 ?
O23 U2 O10 86.4(9) 1_556 3_666 ?
O10 U2 O10 70.6(10) 2_656 3_666 ?
O22 U2 O14 90.6(10) . 1_556 ?
O23 U2 O14 92.1(9) 1_556 1_556 ?
O10 U2 O14 170.7(7) 2_656 1_556 ?
O10 U2 O14 118.5(7) 3_666 1_556 ?
O22 U2 O14 90.6(10) . 4_576 ?
O23 U2 O14 92.1(9) 1_556 4_576 ?
O10 U2 O14 118.5(7) 2_656 4_576 ?
O10 U2 O14 170.7(7) 3_666 4_576 ?
O14 U2 O14 52.4(9) 1_556 4_576 ?
O22 U2 O11 90.5(4) . 2_656 ?
O23 U2 O11 89.3(4) 1_556 2_656 ?
O10 U2 O11 51.9(7) 2_656 2_656 ?
O10 U2 O11 122.5(7) 3_666 2_656 ?
O14 U2 O11 119.0(6) 1_556 2_656 ?
O14 U2 O11 66.6(6) 4_576 2_656 ?
O22 U2 O11 90.5(4) . 3_666 ?
O23 U2 O11 89.3(4) 1_556 3_666 ?
O10 U2 O11 122.5(7) 2_656 3_666 ?
O10 U2 O11 51.9(7) 3_666 3_666 ?
O14 U2 O11 66.6(6) 1_556 3_666 ?
O14 U2 O11 119.0(6) 4_576 3_666 ?
O11 U2 O11 174.3(9) 2_656 3_666 ?
O22 U2 C4 90.2(7) . 2_656 ?
O23 U2 C4 88.4(7) 1_556 2_656 ?
O10 U2 C4 26.2(7) 2_656 2_656 ?
O10 U2 C4 96.8(9) 3_666 2_656 ?
O14 U2 C4 144.7(7) 1_556 2_656 ?
O14 U2 C4 92.3(7) 4_576 2_656 ?
O11 U2 C4 25.7(6) 2_656 2_656 ?
O11 U2 C4 148.7(8) 3_666 2_656 ?
O22 U2 C4 90.2(7) . 3_666 ?
O23 U2 C4 88.4(7) 1_556 3_666 ?
O10 U2 C4 96.8(8) 2_656 3_666 ?
O10 U2 C4 26.2(7) 3_666 3_666 ?
O14 U2 C4 92.3(7) 1_556 3_666 ?
O14 U2 C4 144.7(7) 4_576 3_666 ?
O11 U2 C4 148.7(8) 2_656 3_666 ?
O11 U2 C4 25.7(6) 3_666 3_666 ?
C4 U2 C4 123.0(12) 2_656 3_666 ?
O22 U2 C5 88.7(15) . 1_556 ?
O23 U2 C5 94.3(14) 1_556 1_556 ?
O10 U2 C5 144.7(5) 2_656 1_556 ?
O10 U2 C5 144.7(5) 3_666 1_556 ?
O14 U2 C5 26.3(4) 1_556 1_556 ?
O14 U2 C5 26.3(4) 4_576 1_556 ?
O11 U2 C5 92.8(4) 2_656 1_556 ?
O11 U2 C5 92.8(4) 3_666 1_556 ?
C4 U2 C5 118.5(6) 2_656 1_556 ?
C4 U2 C5 118.5(6) 3_666 1_556 ?
O22 U2 Ca5 87.3(5) . 1_556 ?
O23 U2 Ca5 94.3(5) 1_556 1_556 ?
O10 U2 Ca5 156.4(5) 2_656 1_556 ?
O10 U2 Ca5 85.9(5) 3_666 1_556 ?
O14 U2 Ca5 32.8(4) 1_556 1_556 ?
O14 U2 Ca5 85.1(4) 4_576 1_556 ?
O11 U2 Ca5 151.6(5) 2_656 1_556 ?
O11 U2 Ca5 34.1(5) 3_666 1_556 ?
C4 U2 Ca5 176.3(6) 2_656 1_556 ?
C4 U2 Ca5 59.7(6) 3_666 1_556 ?
C5 U2 Ca5 58.83(10) 1_556 1_556 ?
O24 U3 O25 179.7(14) 1_655 . ?
O24 U3 O16 87.7(10) 1_655 3_666 ?
O25 U3 O16 92.5(11) . 3_666 ?
O24 U3 O16 87.7(10) 1_655 2_656 ?
O25 U3 O16 92.5(11) . 2_656 ?
O16 U3 O16 65.9(12) 3_666 2_656 ?
O24 U3 O19 90.5(10) 1_655 1_655 ?
O25 U3 O19 89.2(11) . 1_655 ?
O16 U3 O19 172.9(8) 3_666 1_655 ?
O16 U3 O19 120.9(8) 2_656 1_655 ?
O24 U3 O19 90.5(10) 1_655 4_675 ?
O25 U3 O19 89.2(11) . 4_675 ?
O16 U3 O19 120.9(8) 3_666 4_675 ?
O16 U3 O19 172.9(8) 2_656 4_675 ?
O19 U3 O19 52.1(10) 1_655 4_675 ?
O24 U3 O15 88.7(5) 1_655 4_575 ?
O25 U3 O15 91.3(5) . 4_575 ?
O16 U3 O15 118.9(8) 3_666 4_575 ?
O16 U3 O15 53.0(8) 2_656 4_575 ?
O19 U3 O15 68.0(8) 1_655 4_575 ?
O19 U3 O15 120.1(8) 4_675 4_575 ?
O24 U3 O15 88.7(5) 1_655 . ?
O25 U3 O15 91.3(5) . . ?
O16 U3 O15 53.0(8) 3_666 . ?
O16 U3 O15 118.9(8) 2_656 . ?
O19 U3 O15 120.1(8) 1_655 . ?
O19 U3 O15 68.0(8) 4_675 . ?
O15 U3 O15 171.6(11) 4_575 . ?
O24 U3 C6 85.8(8) 1_655 3_666 ?
O25 U3 C6 94.3(9) . 3_666 ?
O16 U3 C6 27.6(9) 3_666 3_666 ?
O16 U3 C6 93.4(10) 2_656 3_666 ?
O19 U3 C6 145.3(9) 1_655 3_666 ?
O19 U3 C6 93.4(9) 4_675 3_666 ?
O15 U3 C6 146.1(11) 4_575 3_666 ?
O15 U3 C6 25.5(8) . 3_666 ?
O24 U3 C6 85.8(8) 1_655 2_656 ?
O25 U3 C6 94.3(9) . 2_656 ?
O16 U3 C6 93.4(10) 3_666 2_656 ?
O16 U3 C6 27.6(9) 2_656 2_656 ?
O19 U3 C6 93.4(9) 1_655 2_656 ?
O19 U3 C6 145.3(9) 4_675 2_656 ?
O15 U3 C6 25.5(8) 4_575 2_656 ?
O15 U3 C6 146.1(11) . 2_656 ?
C6 U3 C6 120.6(15) 3_666 2_656 ?
O24 U3 C7 88.4(13) 1_655 1_655 ?
O25 U3 C7 91.3(13) . 1_655 ?
O16 U3 C7 146.8(6) 3_666 1_655 ?
O16 U3 C7 146.8(6) 2_656 1_655 ?
O19 U3 C7 26.2(5) 1_655 1_655 ?
O19 U3 C7 26.2(5) 4_675 1_655 ?
O15 U3 C7 94.0(6) 4_575 1_655 ?
O15 U3 C7 94.0(6) . 1_655 ?
C6 U3 C7 119.2(8) 3_666 1_655 ?
C6 U3 C7 119.2(8) 2_656 1_655 ?
O24 U3 Ca3 96.5(10) 1_655 3_666 ?
O25 U3 Ca3 83.9(11) . 3_666 ?
O16 U3 Ca3 34.1(6) 3_666 3_666 ?
O16 U3 Ca3 34.1(6) 2_656 3_666 ?
O19 U3 Ca3 153.1(5) 1_655 3_666 ?
O19 U3 Ca3 153.1(5) 4_675 3_666 ?
O15 U3 Ca3 86.1(6) 4_575 3_666 ?
O15 U3 Ca3 86.1(6) . 3_666 ?
C6 U3 Ca3 61.4(8) 3_666 3_666 ?
C6 U3 Ca3 61.4(8) 2_656 3_666 ?
C7 U3 Ca3 175.2(8) 1_655 3_666 ?
O3 C1 O2 122(3) 1_556 . ?
O3 C1 O1 123(3) 1_556 . ?
O2 C1 O1 115(3) . . ?
O3 C1 U1 179(2) 1_556 . ?
O2 C1 U1 58.1(16) . . ?
O1 C1 U1 57.7(15) . . ?
O4 C2 O5 121(3) . . ?
O4 C2 O6 125(3) . . ?
O5 C2 O6 113(3) . . ?
O4 C2 U1 168(2) . . ?
O5 C2 U1 55.5(15) . . ?
O6 C2 U1 60.0(15) . . ?
O7 C3 O8 125(3) 3_666 . ?
O7 C3 O9 122(3) 3_666 . ?
O8 C3 O9 113(3) . . ?
O7 C3 U1 170(2) 3_666 . ?
O8 C3 U1 58.6(15) . . ?
O9 C3 U1 55.6(15) . . ?
O7 C3 Ca2 36.2(15) 3_666 3_566 ?
O8 C3 Ca2 90.1(16) . 3_566 ?
O9 C3 Ca2 155(2) . 3_566 ?
U1 C3 Ca2 142.1(11) . 3_566 ?
O11 C4 O10 119(3) . . ?
O11 C4 O12 121(3) . . ?
O10 C4 O12 121(3) . . ?
O11 C4 U2 60.0(15) . 3_666 ?
O10 C4 U2 58.6(15) . 3_666 ?
O12 C4 U2 179(2) . 3_666 ?
O13 C5 O14 125(2) . 4_575 ?
O13 C5 O14 125(2) . . ?
O14 C5 O14 110(5) 4_575 . ?
O13 C5 U2 177(4) . 1_554 ?
O14 C5 U2 55(2) 4_575 1_554 ?
O14 C5 U2 55(2) . 1_554 ?
O15 C6 O17 129(3) 3_666 . ?
O15 C6 O16 116(3) 3_666 . ?
O17 C6 O16 116(3) . . ?
O15 C6 U3 58.2(18) 3_666 3_666 ?
O17 C6 U3 172(3) . 3_666 ?
O16 C6 U3 57.9(18) . 3_666 ?
O18 C7 O19 124.9(19) . 4_575 ?
O18 C7 O19 124.9(19) . . ?
O19 C7 O19 110(4) 4_575 . ?
O18 C7 U3 180(3) . 1_455 ?
O19 C7 U3 55.1(19) 4_575 1_455 ?
O19 C7 U3 55.1(19) . 1_455 ?
O18 C7 Ca4 29(2) . 1_556 ?
O19 C7 Ca4 122.3(19) 4_575 1_556 ?
O19 C7 Ca4 122.3(19) . 1_556 ?
U3 C7 Ca4 151.6(15) 1_455 1_556 ?
C1 O1 Ca2 149(2) . . ?
C1 O1 U1 95.9(18) . . ?
Ca2 O1 U1 113.6(8) . . ?
C1 O2 Ca5 149(2) . 1_556 ?
C1 O2 U1 95.7(19) . . ?
Ca5 O2 U1 115.1(9) 1_556 . ?
C1 O3 Ca4 124.0(19) 1_554 . ?
C2 O4 Ca5 124(2) . 3_666 ?
C2 O5 U1 98.1(18) . . ?
C2 O5 Ca1 143(2) . . ?
U1 O5 Ca1 113.2(8) . . ?
C2 O6 Ca5 154.4(19) . 1_556 ?
C2 O6 U1 92.6(17) . . ?
Ca5 O6 U1 112.4(7) 1_556 . ?
C3 O7 Ca2 126(2) 3_666 1_655 ?
C3 O8 U1 94.8(17) . . ?
C3 O8 Ca2 155.0(18) . . ?
U1 O8 Ca2 108.0(7) . . ?
C3 O9 U1 97.0(18) . . ?
C3 O9 Ca1 144(2) . . ?
U1 O9 Ca1 112.0(8) . . ?
C4 O10 U2 95.2(18) . 3_666 ?
C4 O11 Ca5 154.2(19) . 3_665 ?
C4 O11 U2 94.3(17) . 3_666 ?
Ca5 O11 U2 110.7(8) 3_665 3_666 ?
C4 O12 Ca5 129.8(18) . . ?
C4 O12 Ca1 119.9(18) . . ?
Ca5 O12 Ca1 107.4(8) . . ?
C5 O13 Ca4 140(4) . . ?
C5 O14 Ca5 147(2) . . ?
C5 O14 U2 99(2) . 1_554 ?
Ca5 O14 U2 112.8(8) . 1_554 ?
C6 O15 Ca2 147(2) 3_666 1_655 ?
C6 O15 U3 96(2) 3_666 . ?
Ca2 O15 U3 113.6(9) 1_655 . ?
C6 O16 Ca3 153(2) . . ?
C6 O16 U3 94(2) . 3_666 ?
Ca3 O16 U3 110.5(10) . 3_666 ?
C6 O17 Ca2 131(2) . . ?
C7 O18 Ca4 137(3) . 1_556 ?
C7 O19 U3 99(2) . 1_455 ?
C7 O19 Ca2 149(2) . 4_575 ?
U3 O19 Ca2 109.4(8) 1_455 4_575 ?
Ca1 OW5 Ca5 102.5(7) . . ?
 
_refine_diff_density_max    4.449
_refine_diff_density_min   -1.744
_refine_diff_density_rms    0.360